Enhanced adhesive drywall finish and joint compound and method of use
OwnerSheila Cross, Kory Ehlertinventors
Life of this patent
Estimating the term…
Abstract
The present invention relates to an improved drywall finish and joint compound comprised of a mixture of fractured aluminum oxide, glass bead, calcium sulfate, calcium carbonate, magnesium aluminum phyllosilicate, aluminum silicate hydroxide, polyvinyl acetate, polyvinyl alcohol, metamorphic mineral, sodium bicarbonate, silicon and aluminides, talc, kaolin, and metal oxide. The improved drywall finish and joint compound is capable of adhering to drywall, wood, concrete, brick, stone, steel, and other surfaces, and can be applied using a conventional trowel or similar device, cures quickly, and eliminates the need for taping and bedding. The compound saves extensive time and labor when installing, repairing, or working with drywall.
Claims20
A drywall finishing compound comprising:
- a fractured aluminum oxide;
- a calcium sulfate;
- a calcium carbonate;
- a glass bead;
- a magnesium aluminum phyllosilicate;
- an aluminum silicate hydroxide;
- a polyvinyl acetate;
- a polyvinyl alcohol;
- a sodium bicarbonate;
- a polymer bonder;
- a talc;
- a kaolin;
- a metamorphic mineral;
- a metal oxide;
- a silicon;
- an aluminide;
- and
- an additive.
An drywall finishing compound comprising:
- a fractured aluminum oxide comprising 12-15 percent weight of the drywall finishing compound;
- a calcium sulfate comprising approximately 1 percent weight of the drywall finishing compound;
- a calcium carbonate comprising 2-3 percent weight of the drywall finishing compound;
- a magnesium aluminum phyllosilicate comprising 1-3 percent weight of the drywall finishing compound;
- an aluminum silicate hydroxide comprising 2-4 percent weight of the drywall finishing compound;
- a polyvinyl acetate comprising 10-12 percent weight of the drywall finishing compound;
- a polyvinyl alcohol comprising 9-11 percent weight of the drywall finishing compound;
- a sodium bicarbonate comprising 5-7 percent weight of the drywall finishing compound;
- a polymer bonder comprising 12-15 percent weight of the drywall finishing compound;
- a glass bead comprising 15-20 percent weight of the drywall finishing compound;
- a metamorphic mineral comprising approximately 1 percent weight of the drywall finishing compound;
- a talc comprising 15-20 percent weight of the drywall finishing compound;
- a kaolin comprising 3-6 percent weight of the drywall finishing compound;
- a combination of a metal oxide, a silicon and an aluminide comprising 2-5 percent weight of the drywall finishing compound;
- and
- an additive comprised of a fractured aluminum oxide, a glass material from a group consisting of a glass bead, a fire glass bead and a crushed glass, and a liquid acrylic polymer comprised of a gelatin.
A method of adding an additive to a secondary product, the method comprising the step of:
- adding an additive comprised of a fractured aluminum, a glass, and a liquid acrylic polymer to a secondary product during a manufacturing process of the secondary product.