Method for continuously preparing nano zinc oxide using carbon dioxide

A method for preparing nano zinc oxide using carbon dioxide, comprising:

• step 1, determining experimental materials and experimental instruments, wherein the experimental materials comprise a material containing ZnO, Zn(OH)2, and Zn with ratios of 75%, 17%, and 8% respectively, carbon dioxide, hydrogen peroxide, and deionized water, and the experimental instruments comprise a high-pressure reactor, a high shear emulsification machine, a vacuum pump, a constant temperature oven, and a muffle furnace;
• step 2, preparing a raw material and processing the raw material:
• adding 2000 milliliters (mL) of the deionized water into a beaker with a capacity of 5 liters (L);
• weighting 800 grams (g) of the material containing ZnO, Zn(OH)2, and Zn with ratios of 75%, 17%, and 8% respectively and pouring the material containing ZnO, Zn(OH)2, and Zn with ratios of 75%, 17%, and 8% respectively into the beaker;
• stirring the material containing ZnO, Zn(OH)2, and Zn with ratios of 75%, 17%, and 8% respectively to obtain a dilute zinc slurry with a solid-liquid ratio of the material containing ZnO, Zn(OH)2, and Zn with ratios of 75%, 17%, and 8% respectively to the deionized water being 1:2.5;
• emulsifying the dilute zinc slurry in the high shear emulsifying machine to obtain an emulsified zinc slurry;
• and sieving the emulsified zinc slurry to obtain a preprocessed emulsified zinc slurry;
• step 3, oxidizing the preprocessed emulsified zinc slurry:
• pouring the preprocessed emulsified zinc slurry into the high-pressure reactor;
• adding 160 mL of the hydrogen peroxide into the high-pressure reactor;
• and stirring the preprocessed emulsified zinc slurry at one standard atmospheric pressure for 20 minutes (min) to make zinc pure substance be transformed into zinc hydroxide, and thereby obtaining a zinc-free emulsified zinc hydroxide slurry;
• step 4, carbonizing the zinc-free emulsified zinc hydroxide slurry:
• introducing CO2 gas into the high-pressure reactor and maintaining a pressure in the high-pressure reactor at 0.7 megapascals (MPa) to make the zinc-free emulsified zinc hydroxide slurry and the CO2 gas to perform a carbonization reaction for 110 min, then analyzing a total amount of ZnCO3 generated in the carbonization reaction;
• ending the carbonization reaction when the total amount of ZnCO3 exceeds 80%, otherwise, performing the carbonization reaction until the total amount of ZnCO3 exceeds 80%;
• wherein during the carbonization reaction, a temperature of the carbonization reaction is maintained at 70 Celsius degrees (° C.);
• and a jacket of the high-pressure reactor is configured to provide cooling water to adjust the temperature when the temperature exceeds 70° C.;
• step 5, filtering and washing:
• stopping introducing the CO2 gas after completing the carbonization reaction, releasing the pressure in the high-pressure reactor, taking out a carbonization material from the high-pressure reactor, performing vacuum filtration on the carbonization material to obtain a filter cake, washing the filter cake with the deionized water at least 3 times to obtain a washed filter cake, and reusing a washing liquid obtained after washing the filter cake to prepare the dilute zinc slurry;
• and
• step 6, drying and calcining:
• drying the washed filter cake in the constant temperature oven for 4 hours to obtain dried basic zinc carbonate, wherein a mass fraction of water in the dried basic zinc carbonate is less than 1%;
• calcining the dried basic zinc carbonate in the muffle furnace for 120 min to obtain zinc oxide, cooling the zinc oxide to obtain cooled nano zinc oxide, crushing and sieving the cooled zinc oxide to obtain nano zinc oxide.