Nickel-plated stainless steel sheet having excellent processability and manufacturing method thereof

A nickel-plated stainless steel plate, comprising:

• a stainless steel base plate;
• and
• a nickel (Ni) plating layer formed on at least one surface of the stainless steel base plate by electroplating,
• wherein the stainless steel base plate contains, based on its total weight, C at about 0.001 wt % to about 1.5 wt %, Si at more than 0 wt % to about 2.0 wt %, Mn at about 0.1 wt % to about 2.5 wt %, P at more than 0 wt % to about 0.5 wt %, S at more than 0 wt % to about 0.3 wt %, Cr at about 8 wt % to about 20 wt %, and the remainder being Fe and inevitable impurities, and
• the nickel (Ni) plating layer includes a strike plating layer and a main plating layer containing a first plating layer and a second plating layer,
• in which
• (i) the strike plating layer, the first plating layer, and the second plating layer are sequentially laminated on the one surface of the stainless steel base plate;
• (ii) the strike plating layer has a thickness of about 0.3 μm to about 0.5 μm;
• (iii) the first plating layer, having a thickness of about 0.5 μm to about 2.5 is both an electrolytic nickel plating layer and a matte plating layer;
• and
• (iv) the second plating layer, having a thickness of about 0.3 μm to about 1.5 is both an electrolytic nickel plating layer and a semi-bright plating layer.