Composition for material for liquid metal deposition or additive manufacturing, method and product

A metallic powder mixture, usable for build up via liquid metal deposition or any additive manufacturing method, comprising (in wt %):

• a nickel (Ni) based superalloy with a content of 20% to 60%,
• a NiCoCrAlY-composition with a content of 70% to 30% and
• a metallic braze material with a content between 10% to 5%,
• wherein the melting point of the braze material is at least 10K lower than the melting point of the nickel based superalloy,
• wherein the nickel (Ni) based superalloy comprises (in wt %):
• Nickel (Ni)
• 61.6%
• Carbon (C)
• 0.08%
• Chromium (Cr)
• 8.25%
• Molybdenum (Mo)
• 0.50%
• Tungsten (W)
• 9.50%
• Titan (Ti)
• 0.75%
• Aluminum (Al)
• 5.55%
• Boron (B)
• 0.02%
• Tantalum (Ta)
• 3.20%
• Hafnium (Hf)
• 1.30%,
• no Yttrium (Y) and/or
• no Rhenium (Re)
• wherein the NiCoCrAlY composition comprises (in wt %):
• 14%-22%
• Chromium (Cr)
• 9.0%-11.5%
• Aluminum (Al)
• 0.3%-0.5%
• Yttrium (Y)
• 11%-26%
• Cobalt (Co)
• 0%-1.0%
• Silicon (Si),
• 0%-2.5%
• Rhenium (Re)
• and remainder Nickel (Ni).