US 11,299,658 B2Granted
Condensation-curable polyethersilicone tile adhesives
AssigneeWacker Chemie AG
InventorsDaniel J. Mania, Jerry Havens
Life of this patent
Estimating the term…
Abstract
Tiles are adhesively bonded to substrates such as kitchen or bathroom walls by a process in which a tile adhesive is used, the tile adhesive being a one component RTV-1 moisture-curable tile adhesives having properties superior to conventional cementitious and RTU tile adhesives, which contain at least one low viscosity alkoxysilyl-functional polymer, a silicone resin, an aminoalkyl-functional alkoxysilane or partial hydrolysate thereof, and in excess of 60 weight percent mineral filler, of which at least 50 weight percent is a non-reinforcing filler.
Claims18
In a process for adhesively bonding inorganic facing materials to a substrate with a tile adhesive, the improvement comprising employing an RTV single component (RTV-1) tile adhesive composition, wherein the tile adhesive composition is prepared by admixing:
- a) from 5 to 40 weight percent of a moisture-curable alkoxysilyl-functional polymer component based on the total weight of the tile adhesive;
- and
- b) a filler component comprising sand having a BET surface area of less than 30 m2/g, wherein the amount of the filler component is such that the sand is present in an amount of at least 60 wt. % based on the total weight of the tile adhesive;
- wherein the polymer component comprises:
- A) 100 parts of at least one liquid alkoxysilyl-functional polymer having a viscosity of less than 700 Pas measured at 25° C., and corresponding to the formula (I)
- X—[(CR12)b—SiRa(OR2)3-a]x (I),
- wherein
- X denotes an x-valent polymer radical bonded to carbon of the (CR12)b group via a urea or urethane group
- R are identical or different and are monovalent, optionally substituted, SiC-bonded hydrocarbon radicals,
- R1 are identical or different and are hydrogen or a monovalent, optionally substituted hydrocarbon radical, which may be bonded to carbon via nitrogen, phosphorus, oxygen, sulfur, or carbonyl group,
- R2 are identical or different and are hydrogen or a monovalent, optionally substituted hydrocarbon radical,
- x is an integer from 1 to 10,
- a each is identical or different and is 0, 1, or 2,
- b each is identical or different and is an integer from 1 to 10,
- B) from 40 to 1000 parts relative to 100 parts A, of at least one silicone resin comprising units of the formula (V)
- R3c(R4O)dSiO(4-c-d)/2 (V),
- where
- R3 are identical or different and denotes hydrogen or a monovalent, SiC-bonded, optionally substituted hydrocarbon radical,
- R4 are identical or different and denotes hydrogen or a monovalent, optionally substituted hydrocarbon radical,
- c is 0, 1, 2, or 3, and
- d is 0, 1, 2, or 3,
- where the sum of c+d is less than or equal to 3 and in at least 50% of the units of the formula (V) c is equal to 0 or 1,
- C) at least 0.5 parts per 100 parts (A) of at least one aminoalkylalkoxysilane or partial hydrolysate thereof
- D) optionally, one of more condensation catalysts;
- E) optionally, one or more water scavengers;
- F) optionally, one or more adhesion promoters different from the aminoalkylalkoxysilane or partial hydrolysate thereof, and different from components C) and E);
- G) optionally one or more plasticizers;
- H) optionally, one or more alkoxysilyl-functional crosslinkers different from components E) and F) and having a molecular weight below 500 Da, and/or a partial hydrolysate thereof;
- I) optionally, one or more antioxidants and/or UV-stabilizers;
- J) optionally, one or more biocides.
27 more elements
In a process for adhesively bonding inorganic facing materials to a substrate with a tile adhesive, the improvement comprising employing an RTV single component (RTV-1) tile adhesive composition, wherein the tile adhesive composition is prepared by admixing:
- a) from 5 to 40 weight percent of a moisture-curable alkoxysilyl-functional polymer component based on the total weight of the tile adhesive;
- and
- b) a filler component comprising sand, wherein the amount of the filler component is such that sand is present in an amount of at least 60 wt. % based on the total weight of the tile adhesive;
- wherein the polymer component comprises:
- A) 100 parts of at least one liquid alkoxysilyl-functional polymer having a viscosity of less than 700 Pa·s measured at 25° C., and corresponding to the formula (I)
- X—[(CR12)b—SiRa(OR2)3-a]x (I),
- wherein
- X denotes an x-valent polymer radical bonded to carbon of the (CR12)b group via a urea or urethane group
- R are identical or different and are monovalent, optionally substituted, SiC-bonded hydrocarbon radicals,
- R1 are identical or different and are hydrogen or a monovalent, optionally substituted hydrocarbon radical, which may be bonded to carbon via nitrogen, phosphorus, oxygen, sulfur, or carbonyl group,
- R2 are identical or different and are hydrogen or a monovalent, optionally substituted hydrocarbon radical,
- x is an integer from 1 to 10,
- a each is identical or different and is 0, 1, or 2,
- b each is identical or different and is an integer from 1 to 10,
- B) from 40 to 1000 parts relative to 100 parts A, of at least one silicone resin comprising units of the formula (V)
- R3c(R4O)dSiO(4-c-d)/2 (V),
- where
- R3 are identical or different and denotes hydrogen or a monovalent, SiC-bonded, optionally substituted hydrocarbon radical,
- R4 are identical or different and denotes hydrogen or a monovalent, optionally substituted hydrocarbon radical,
- c is 0, 1, 2, or 3, and
- d is 0, 1, 2, or 3,
- where the sum of c+d is less than or equal to 3 and in at least 50% of the units of the formula (V) c is equal to 0 or 1,
- C) at least 0.5 parts per 100 parts (A) of at least one aminoalkylalkoxysilane or partial hydrolysate thereof
- D) optionally, one of more condensation catalysts;
- E) optionally, one or more water scavengers;
- F) optionally, one or more adhesion promoters different from the aminoalkylalkoxysilane or partial hydrolysate thereof, and different from components C) and E);
- G) optionally one or more plasticizers;
- K) optionally, one or more alkoxysilyl-functional crosslinkers different from components E) and F) and having a molecular weight below 500 Da, and/or a partial hydrolysate thereof;
- L) optionally, one or more antioxidants and/or UV-stabilizers;
- M) optionally, one or more biocides,
- wherein the sand has a sieve size of from 0.037 mm to 1.0 mm.
28 more elements
Dependencies are inferred from the claim text.