Magnesium oxide based dielectric ceramics with ultrahigh dielectric breakdown strength and its preparation method
AssigneeShanghai Institute of Ceramics, Chinese Academy of Sciences
InventorsXianlin Dong, Chi Zhang, Ying Chen
Life of this patent
Estimating the term…
Abstract
The present application relates to a magnesium oxide based dielectric ceramics with ultrahigh dielectric breakdown strength and a preparation method thereof. The composition of the magnesium oxide based dielectric ceramic material comprises: (1−x)MgO—xAl2O3, wherein 0<x≤0.12 and x is a mole percentage. The material has a specific composite structure with magnesium aluminate spinel acting as a second phase surrounding a principal crystalline phase, MgO.
Claims2
A magnesium oxide based dielectric ceramic material, having a composition of (1−x)MgO—xAl2O3, wherein 0.08≤x≤0.1 and x is a mole percentage, and having a composite structure with magnesium aluminate spinel acting as a second phase surrounding a principal crystalline phase, MgO;
- wherein the magnesium oxide based dielectric ceramic material has a dielectric breakdown strength of 111.5 to 126.4 kV/mm and a surface flashover strength of 74.3 to 78.7 kV/cm;
- and
- wherein the magnesium oxide based dielectric ceramic material is prepared by a method including:
- weighing and mixing magnesia and alumina according to the composition of the magnesium oxide based dielectric ceramic material to obtain mixed powders, wherein the magnesia is light-burnt magnesia obtained by calcining magnesium source at a temperature of 800 to 1,000° C. for a period of 2 to 6 hours;
- preparing a green body from the mixed powders;
- and
- sintering the green body at a temperature of 1,500 to 1,550° C. for a period of 1 to 3 hours to obtain the magnesium oxide based dielectric ceramic material having the composition of (1−x)MgO—xAl2O3.
Dependencies are inferred from the claim text.