Thermoplastic resin-coated metal sheet, can body and can lid made from the same metal sheet

A seamless can formed from a thermoplastic resin-coated metal sheet obtained by coating at least one surface of a metal sheet with a thermoplastic resin coating via an intervening polyester primer layer comprising a polyester primer, wherein

• said polyester primer comprises a polyester resin and a curing agent,
• said polyester resin consists of 50 mol % of dicarboxylic acid components and 50 mol % of diol components,
• the dicarboxylic acid components consist of sebacic acid, isophthalic acid, and optionally terephthalic acid, where the sebacic acid is contained in an amount of 8 to 16.2 mol %, the isophthalic acid is contained in an amount of 15 to 40 mol %, and the terephthalic acid is contained in an amount of 0 to 18.8 mol % based on the total amount of dicarboxylic acid components and diol components of the polyester resin, and
• the diol components consist of cyclohexanedimethanol and at least one of ethylene glycol or propylene glycol, where the cyclohexanedimethanol is contained in an amount of 17.7 to 30 mol % and the ethylene glycol and/or the propylene glycol is contained in an amount of greater than 0 to 30 mol % based on the total amount of dicarboxylic acid components and diol components of the polyester resin,
• said curing agent being at least one selected from the group consisting of a phenol resin, an isocyanate compound, and an amino resin, and being contained in an amount of 5 to 15 parts by mass per 100 parts by mass of said polyester resin,
• said polyester primer layer has a thickness in a range of 0.4 to 2.7 μm,
• said polyester primer, when prepared for testing in the form of a 10 μm thick dry primer sheet, has a breaking elongation in a range of 10 to 50% at a tension speed of 1,000 mm/min and an MEK extractability in a range of 9 to 27%,
• said thermoplastic resin coating comprises a polyester film and has a thickness in a range of 5 to 40 μm, and
• said thermoplastic resin coating is formed in two layers including a lower layer and an upper layer, the lower layer comprises a polyester resin based on an ethylene terephthalate unit containing 1 to 30 mol % of at least one of isophthalic acid or naphthalenedicarboxylic acid, and the upper layer comprises a polyester resin based on an ethylene terephthalate unit containing isophthalic acid or naphthalenedicarboxylic acid in an amount smaller than the amount of the isophthalic acid or the naphthalene dicarboxylic acid contained in the lower layer.