Polypropylene fiber and method for manufacturing polypropylene fiber

Abstract

Obtained is a polypropylene fiber that selectively satisfies any of the following requirements: the degree of amorphous orientation being not lower than 85%; the degree of crystalline orientation being not lower than 90%; the degree of crystallinity being 60-75%; the strength being not lower than 7 cN/dtex; the initial elastic modulus being not lower than 100 cN/dtex; the rupture elongation being 10-30%; and the single fiber fineness being 3-20 dtex. This polypropylene fiber, in which a crystalline chain and an amorphous chain are highly oriented and that has high strength and high initial elastic modulus, is produced through a two-stage drawing method and by controlling the drawing tension of the final stage while maintaining production speed.