Forged component, method for manufacturing the same, and connecting rod

A forged component having a chemical composition consisting of, by mass %, C:

• 0.30 to 0.45%, Si:
• 0.05 to 0.35%, Mn:
• 0.50 to 0.90%, P:
• 0.030 to 0.070%, S:
• 0.040 to 0.070%, Cr:
• 0.01 to 0.50%, Al:
• 0.001 to 0.050%, V:
• 0.25 to 0.35%, N:
• 0.0150% or less, and the balance being Fe and unavoidable impurities, and satisfying the following formula 1:
• [C]−4×[S]+[V]−25×[Ca]<0.44 (Formula 1)
• wherein [X] means a value of the content (mass %) of an element X),
• wherein a metal structure of the forged component is a ferrite pearlite structure, and
• a ferrite area ratio is 30% or more;
• a Vickers hardness of the forged component is in the range of 320 to 380 HV;
• a 0.2% yield strength of the forged component is 800114 Pa or more;
• and
• a Charpy V-notch impact value of the forged component is in the range of 7 to 15 J/cm2.