Ink composition for high-speed screen printing, printed article obtained by high-speed printing of said ink composition, and method for producing said printed article

An ink composition for high quality/high definition high-speed screen printing, the ink composition comprising:

• at least one solvent having a boiling point of not less than 170° C. and that is selected from the group consisting of isophorone, a dibasic acid ester (DBE), 3-methoxy-3-methylbutanol, 3-methoxy-3-methylbutyl acetate, ethyleneglycol monobutyl ether acetate, coal tar naphtha, diethyleneglycol monoethyl ether, diethyleneglycol monoethyl ether acetate, diethyleneglycol monobutyl ether, diethyleneglycol monobutyl ether acetate, triethyleneglycol monobutyl ether, triethyleneglycol monobutyl ether acetate, 1,6-hexanediol di(meth)acrylate, dipentaerythritol hexa(meth)acrylate, a vinyl ether monomer, and an amide monomer, wherein the amount of the at least one solvent having a boiling point of not less than 170° C. is not less than 70 wt % of a total weight of all solvent in the ink composition;
• and
• a prepolymer or polymer with a weight-average molecular weight in the range of 2000 to 100,000, in an amount in the range of 15 wt % to 70 wt % with respect to a total weight of the ink composition, the prepolymer or polymer being selected from the group consisting of polyester resins, vinyl chloride-vinyl acetate copolymer resins, butyral resins, polyether-urethane resins, polyester-urethane resins, polycarbonate-urethane resins, epoxy resins, phenol resins, acrylic resins, polyamide resins, polyamideimide resins, polyolefin resins, chlorinated polyolefin resins, chlorinated rubber, melamine resins, urea resins, modified cellulose resins, rosin resins, maleic acid resins, natural resins, alkyd resins, and combinations thereof,
• wherein:
• the ink composition has:
• a viscosity of not less than 6 Pa·s and less than 30 Pa·s as measured with a BH-type rotating viscosimeter at 25° C.,
• a thixotropic index (TI Value) of 2.0 to 8.0, and
• a measured flow radius value of 14.0 to 24.0 mm after 1 minute from a start of measurement by a flow property measuring method using a spread meter at 25° C. according to JIS K5701-1:2000,
• the ink composition satisfies “F60”−“F45”≤0.8 mm, where “F60” is defined as the measured flow radius value after 1 minute and “F45” is defined as the measured flow radius value after 45 seconds from the start of measurement by the flow property measuring method using the spread meter, and
• the ink composition is adapted to produce printed matter in a single step comprising a combination of solid patterns and fine patterns with a printed image edge spreading width of no more than 10 μm from printed image design dimensions of a printing plate, when producing printed matter by screen printing onto an object to be printed using a screen printing plate made by flat working a photosensitive emulsion film on a 355 mesh/inch polyester mesh printing plate, at a squeegee speed of 400 mm/sec, the object to be printed being a flat base material selected from the group consisting of art paper, coated paper, synthetic paper, polyester, polycarbonate, acryl, polypropylene, polyethylene, vinyl chloride, and glass.

An ink composition for high quality/high definition high-speed screen printing, the ink composition comprising:

• at least one solvent having a boiling point of not less than 170° C. and that is selected from the group consisting of isophorone, a dibasic acid ester (DBE), 3-methoxy-3-methylbutanol, 3-methoxy-3-methylbutyl acetate, ethyleneglycol monobutyl ether acetate, coal tar naphtha, diethyleneglycol monoethyl ether, diethyleneglycol monoethyl ether acetate, diethyleneglycol monobutyl ether, diethyleneglycol monobutyl ether acetate, triethyleneglycol monobutyl ether, triethyleneglycol monobutyl ether acetate, 1,6-hexanediol di(meth)acrylate, dipentaerythritol hexa(meth)acrylate, a vinyl ether monomer, and an amide monomer, wherein the amount of the at least one solvent having a boiling point of not less than 170° C. is not less than 70 wt % of a total weight of all solvent in the ink composition;
• a prepolymer or polymer with a weight-average molecular weight in the range of 2000 to 100,000, in an amount in the range of 7 wt % to 70 wt % with respect to a total weight of the ink composition, the prepolymer or polymer being selected from the group consisting of polyester resins, vinyl chloride-vinyl acetate copolymer resins, butyral resins, polyether-urethane resins, polyester-urethane resins, polycarbonate-urethane resins, epoxy resins, phenol resins, acrylic resins, polyamide resins, polyamideimide resins, polyolefin resins, chlorinated polyolefin resins, chlorinated rubber, melamine resins, urea resins, modified cellulose resins, rosin resins, maleic acid resins, natural resins, alkyd resins, and combinations thereof;
• and
• an extender pigment dispersed in the ink composition with a mean particle size of no greater than 35 μm in an amount in the range of 10 wt % to 30 wt % with respect to the total weight of the ink composition,
• wherein:
• the ink composition has:
• a viscosity of not less than 6 Pa·s and less than 30 Pa·s as measured with a BH-type rotating viscosimeter at 25° C.,
• a thixotropic index (TI Value) of 2.0 to 8.0, and
• a measured flow radius value of 14.0 to 24.0 mm after 1 minute from a start of measurement by a flow property measuring method using a spread meter at 25° C. according to JIS K5701-1:2000,
• the ink composition satisfies “F60”−“F45”≤0.8 mm, where “F60” is defined as the measured flow radius value after 1 minute and “F45” is defined as the measured flow radius value after 45 seconds from the start of measurement by the flow property measuring method using the spread meter,
• the ink composition is adapted to produce printed matter in a single step comprising a combination of solid patterns and fine patterns with a printed image edge spreading width of no more than 10 μm from printed image design dimensions of a printing plate, when producing printed matter by screen printing onto an object to be printed using a screen printing plate made by flat working a photosensitive emulsion film on a 355 mesh/inch polyester mesh printing plate, at a squeegee speed of 400 mm/sec, the object to be printed being a flat base material selected from the group consisting of art paper, coated paper, synthetic paper, polyester, polycarbonate, acryl, polypropylene, polyethylene, vinyl chloride, and glass.

An ink composition for high quality/high definition high-speed screen printing, the ink composition comprising:

• at least one solvent having a boiling point of not less than 170° C. and that is selected from the group consisting of isophorone, a dibasic acid ester (DBE), 3-methoxy-3-methylbutanol, 3-methoxy-3-methylbutyl acetate, ethyleneglycol monobutyl ether acetate, coal tar naphtha, diethyleneglycol monoethyl ether, diethyleneglycol monoethyl ether acetate, diethyleneglycol monobutyl ether, diethyleneglycol monobutyl ether acetate, triethyleneglycol monobutyl ether, triethyleneglycol monobutyl ether acetate, 1,6-hexanediol di(meth)acrylate, dipentaerythritol hexa(meth)acrylate, a vinyl ether monomer, and an amide monomer, wherein the amount of the at least one solvent having a boiling point of not less than 170° C. is not less than 70 wt % of a total weight of all solvent in the ink composition;
• and
• a prepolymer or polymer with a weight-average molecular weight in the range of 2000 to 100,000, in an amount in the range of 7 wt % to 70 wt % with respect to a total weight of the ink composition, the prepolymer or polymer being selected from the group consisting of polyester resins, vinyl chloride-vinyl acetate copolymer resins, butyral resins, polyether-urethane resins, polyester-urethane resins, polycarbonate-urethane resins, epoxy resins, phenol resins, acrylic resins, polyamide resins, polyamideimide resins, polyolefin resins, chlorinated polyolefin resins, chlorinated rubber, melamine resins, urea resins, modified cellulose resins, rosin resins, maleic acid resins, natural resins, alkyd resins, and combinations thereof,
• wherein:
• the ink composition has:
• a viscosity of not less than 6 Pa·s and less than 30 Pa·s as measured with a BH-type rotating viscosimeter at 25° C.,
• a thixotropic index (TI Value) of 2.0 to 8.0, and
• a measured flow radius value of 14.0 to 24.0 mm after 1 minute from a start of measurement by a flow property measuring method using a spread meter at 25° C. according to JIS K5701-1:2000,
• the ink composition satisfies “F60”−“F45”≤0.8 mm, where “F60” is defined as the measured flow radius value after 1 minute and “F45” is defined as the measured flow radius value after 45 seconds from the start of measurement by the flow property measuring method using the spread meter,
• the ink composition is adapted to produce printed matter in a single step comprising a combination of solid patterns and fine patterns with a printed image edge spreading width of no more than 10 μm from printed image design dimensions of a printing plate, when producing printed matter by screen printing onto an object to be printed using a screen printing plate made by flat working a photosensitive emulsion film on a 355 mesh/inch polyester mesh printing plate, at a squeegee speed of 400 mm/sec, the object to be printed being a flat base material selected from the group consisting of art paper, coated paper, synthetic paper, polyester, polycarbonate, acryl, polypropylene, polyethylene, vinyl chloride, and glass, and
• the ink composition does not comprise a filler having a conductive property.