Method of manufacturing a ceramic substrate
AssigneeNgk Spark Plug Co., Ltd.
InventorsTatsuya Katoh, Masanori Ito, Masaki Kutsuna
Life of this patent
Estimating the term…
Abstract
A method of manufacturing a ceramic substrate includes the steps of preparing a ceramic paste in which a powder of at least one of a metal boride and a metal silicide is added to a raw material powder of a glass ceramic, applying the ceramic paste to a green sheet which is to become a ceramic layer after firing, applying a conductor paste which is to become a conductor trace after firing to the ceramic paste having been applied to the green sheet, and firing the green sheet carrying the ceramic paste and the conductor paste applied thereto.
Claims4
A method of manufacturing a ceramic substrate including a ceramic layer mainly formed of a glass ceramic and a conductor trace mainly formed of silver (Ag), comprising:
- a step of preparing a ceramic paste in which a powder of at least one of a metal boride and a metal silicide is added to a raw material powder of the glass ceramic, the raw material powder of the glass ceramic comprising borosilicate glass powder and alumina (Al2O3) powder;
- a step of applying the ceramic paste to a green sheet which is to become the ceramic layer after firing;
- a step of applying a conductor paste which is to become the conductor trace after firing to the ceramic paste having been applied to the green sheet;
- and
- a step of firing the green sheet carrying the ceramic paste and the conductor paste applied thereto;
- wherein a total amount of the at least one of the metal boride and the metal silicide with respect to an amount of an inorganic component of the ceramic paste is 3 vol. % to 7 vol. % such that diffusion of a silver component of the conductor trace is prevented.
A method of manufacturing a ceramic substrate including a ceramic layer mainly formed of a glass ceramic and a conductor trace mainly formed of silver (Ag), comprising:
- a step of preparing a ceramic slurry in which a powder of at least one of a metal boride and a metal silicide is added to a raw material powder of the glass ceramic, the raw material powder of the glass ceramic comprising borosilicate glass powder and alumina (Al2O3) powder;
- a step of making from the ceramic slurry a green sheet which is to become the ceramic layer after firing;
- a step of applying a conductor paste which is to become the conductor trace after firing to the green sheet;
- and
- a step of firing the green sheet carrying the conductor paste applied thereto;
- wherein, a total amount of the at least one of the metal boride and the metal silicide with respect to an amount of an inorganic component of the ceramic slurry is 3 vol. % to 7 vol. % such that diffusion of a silver component of the conductor trace is prevented.
Dependencies are inferred from the claim text.