US 10,370,747 B2 · Nitrided component

Abstract

A nitrided component has a chemical composition consisting of, by mass percent, C: 0.07-0.14%, Si: 0.10-0.30%, Mn: 0.4-1.0%, S: 0.005-0.030%, Cr: 1.0-1.5%, Mo: ≤0.05% (including 0%), Al: 0.010% or more to less than 0.10%, V: 0.10-0.25%, optionally at least one element selected from Cu: ≤0.30% and Ni: ≤0.25%, [0.61Mn+1.11Cr+0.35Mo+0.47V≤2.30], and the balance of Fe and impurities. P, N, Ti and O among the impurities are P: ≤0.030%, N: ≤0.008%, Ti: ≤0.005%, and O: ≤0.0030%. The nitrided composition is suitable for use as an automobile ring gear. The nitrided component has a surface hardness of 650-900 HV, core hardness being ≥150 HV, effective case depth of ≥0.15 mm, has excellent bending fatigue strength and surface fatigue strength although the content of Mo is as low as ≤0.05% and has a small amount of expansion caused by nitriding.

Claims2

Dependent claims

A nitrided component having a chemical composition consisting of, by mass percent, C:

0.07 to 0.14%, Si:
0.10 to 0.30%, Mn:
0.4 to 1.0%, S:
0.005 to 0.030%, Cr:
1.0 to 1.5%, Mo:
0.05% or less (including 0%), Al:
0.010% or more to less than 0.10%, and V:
0.10 to 0.25%, Fn1 expressed by Formula (1) is 2.30 or less, and the balance of Fe and impurities, wherein P, N, Ti and O among the impurities are P:
0.030% or less, N:
0.008% or less, Ti:
0.005% or less, and O:
0.0030% or less, in which the surface hardness is 650 to 900 in Vickers hardness, the core hardness is 150 or higher in Vickers hardness, and the effective case depth is 0.15 mm or larger:
Fn1=0.61Mn+1.11Cr+0.35Mo+0.47V (1)
where, the symbol of each element in Formula (1) represents the content thereof in mass percent.