Methods and apparatus for depositing silicon oxide on metal layers

Abstract

Thin layer of silicon oxide is deposited on a substrate having an exposed layer of metal (e.g., W, Cu, Ti, Co, Ta) without causing substantial oxidation of the metal. The method involves: (a) contacting the substrate having an exposed metal layer with a silicon-containing precursor and adsorbing the precursor on the substrate; (b) removing the unadsorbed precursor from a process chamber; and (c) contacting the adsorbed precursor with a plasma formed in a process gas comprising an oxygen source (e.g., O2, CO2, N2O, O3) and H2, to form silicon oxide from the silicon-containing precursor while suppressing metal oxidation. These steps can be repeated until a silicon oxide film of a desired thickness is formed. In some embodiments, the silicon oxide film is used to improve nucleation of subsequently deposited silicon carbide.