US 10,119,200 B2 · Silicon carbide single crystal substrate and process for producing same

Abstract

Provided are: a silicon carbide single crystal substrate which is cut out from a silicon carbide bulk single crystal grown by the Physical Vapor Transport method; and a process for producing the same. The number of screw dislocations in one of the semicircle areas of the substrate is smaller than that in the other thereof, namely, the number of screw dislocations in a given area of the substrate is reduced. The semicircle areas of the substrate correspond respectively to the halves of the substrate. The present invention pertains to: a silicon carbide single crystal substrate which is cut out from a silicon carbide bulk single crystal grown by the Physical Vapor Transport method and which is characterized in that the average value of the screw-dislocation densities observed at multiple measurement points in one of the semicircle areas, which correspond respectively to the halves of the substrate, is 80% or less of the average value of screw-dislocation densities observed at multiple measurement points in the other of the semicircle areas; and a process for producing the same.

Claims4

Dependent claims

A method for manufacturing a silicon carbide single crystal by a physical vapor transport method using a seed crystal, the method being characterized by including:

(i) a first growth step of growing a silicon carbide single crystal having a thickness of at least 1 mm at a first growth atmosphere pressure of not lower than 0.13 kPa and not higher than 2.6 kPa and a first growth temperature in which the temperature of the seed crystal is not lower than 2100° C. and not higher than 2400° C.;
(ii) a second growth step of growing the silicon carbide single crystal having a thickness of at least 0.5 mm at a second growth atmosphere pressure of higher than 2.6 kPa and not higher than 65 kPa and a second growth temperature in which the temperature of the seed crystal is not lower than 2100° C. and not higher than 2400° C.;
and
(iii) a third growth step of growing the silicon carbide single crystal to a larger thickness than in the first growth step at a third growth atmosphere pressure of not lower than 0.13 kPa and not higher than 2.6 kPa and a third growth temperature in which the temperature of the seed crystal is not lower than 2100° C. and not higher than 2400° C.;
wherein the seed crystal is composed of SiC single crystal and has an off angle θs of more than 0° and not more than 16° relative to (0001) plane,
wherein a constant growth temperature is maintained throughout the steps (i) to (iii).

3 more elements

Dependencies are inferred from the claim text.

Silicon carbide single crystal substrate and process for producing same

Life of this patent

Silicon carbide single crystal substrate and process for producing same

Life of this patent

Abstract

Claims4