Back to results
US 10,047,252 B2Granted
Extrudable pressure sensitive non-black adhesive composition and methods for preparing the same
AssigneeFirestone Building Products Company, LLC
InventorsJiansheng Tang, Brandon Ward
Life of this patent
Estimating the term…
Abstract
A pressure-sensitive adhesive polymeric composition comprising: a butyl rubber; a polyurethane; an olefinic polymer component; and a filler that includes titanium dioxide, wherein said adhesive polymeric composition is pressure-sensitive, and where pressure-sensitive adhesive polymeric composition is a solids composition wherein said butyl rubber forms a matrix.
Claims10
A method for producing a pressure-sensitive adhesive polymeric composition, the method comprising:
- (a) providing a butyl rubber including one or more halogen atoms and one or more double bonds;
- (b) providing an olefinic polymer or copolymer;
- (c) providing a filler that includes titanium dioxide;
- (d) providing a phenolic resin having a plurality of hydroxyl groups;
- (e) mixing (a), (b), (c), and (d), and optionally, one or more ingredients selected from the group consisting of oils and tackifying resins, to allow the butyl rubber to react with the phenolic resin, to provide butyl rubber having at least one hydroxyl group;
- (f) providing an isocyanate;
- (g) mixing to allow the isocyanate to react with the at least one hydroxyl group of the butyl rubber, to form a butyl rubber having at least one urethane group;
- and
- (h) further mixing to allow the isocyanate to react with the phenolic resin, to form a polyurethane in the presence of the butyl rubber having at least one urethane group, the filler, and the olefinic polymer or copolymer.
6 more elements
A method for producing a pressure-sensitive adhesive polymeric composition, the method comprising:
- (a) charging a halogenated butyl rubber, an olefinic polymer or copolymer, an unfunctionalized phenolic resin, a filler that includes titanium dioxide, and optionally, one or more ingredients selected from the group consisting of oils, tackifying resins, and catalysts to a reaction extruder;
- (b) mixing to allow at least partial crosslinking of said halogenated butyl rubber, wherein said step of mixing optionally includes adding oil;
- (c) charging isocyanate;
- (d) optionally, charging one or more oil;
- and
- (e) mixing to form a phenolic resin-based polyurethane, wherein said phenolic resin-based polyurethane and said olefinic polymer or copolymer are dispersed within said at least partially crosslinked halogenated butyl rubber.
3 more elements
Dependencies are inferred from the claim text.