Method of recovering metals from spent li-ion batteries
AssigneeAttero Recycling Pvt. Ltd.
InventorsNitin Gupta, G. Prabaharan, Smruti Prakash Barik, Bhuvnesh Kumar
Life of this patent
Estimating the term…
Abstract
The present invention relates to an improved process and method of recovering metals of value from used Lithium Ion batteries. More particularly, the invention provides a method for recovering cobalt and lithium along with other metals of value wherein the method includes physical processes for separation, limiting the use of chemical for removing minor impurities. Majority of elements were separated by physical processes instead of chemical processes which gives the benefit of cost saving in chemical treatment of liquid and solid effluents. The invention provides for a cost effective, economic and environmental friendly process for recovering metals of value.
Claims18
A process for recovering valuable metals from spent lithium ion batteries comprising the steps of:
- a) shredding the lithium ion batteries into particles of a preferable size, in water, with water level well above the level of the batteries being shredded to obtain a slurry and shredded plastic and polymer matrix;
- b) removing the plastic and polymer matrix that floats on the water in step a);
- c) wet screening the slurry obtained in step a) through sieve of 50 mesh to separate particles based on sizes wherein coarser particles containing copper, aluminum and protection circuit modules form screened slurry containing solids are retained by the sieve and collected, and finer particles containing lithium and cobalt are aggregated;
- d) filtering the lithium and cobalt containing aggregate of step c) through a filter press to obtain a wash liquor containing lithium and a residue containing cobalt, metal impurities and organic matrix;
- e) drying the residue of step d) and roasting the dried residue at 900° C. to obtain cobalt oxide;
- f) washing and filtering the cobalt oxide of step e) with dilute acid solution at pH range 2.0 to 3.0 to obtain pure cobalt oxide and filtrate;
- g) treating the wash liquor of step d) with saturated solution of soda ash at pH range 11 to 11.5 and temperature ranging from 80 to 120° C. for 3-6 hours to obtain lithium carbonate precipitate and supernatant.
A method for recovering valuable metals from spent lithium-ion batteries comprising:
- wet shredding the lithium-ion batteries to obtain a slurry, and shredded plastic and polymer matrix;
- wet sieving the slurry so that coarse particles including copper, aluminum, and protection circuit modules are retained by a sieve, and a liquid, including dissolved lithium, and fine particles of cobalt, passes through the sieve;
- filtering the liquid to obtain a wash liquor, including dissolved lithium, and a residue including cobalt, metal impurities, and organic matrix;
- and
- treating the wash liquor with a saturated solution of soda ash at a pH between 11 and 11.5 to obtain lithium carbonate precipitate and a supernatant liquid, wherein the wash liquor is treated with the saturated solution of soda ash at a temperature between 80° C. and 120° C. for 3 hours to 6 hours.
Dependencies are inferred from the claim text.