Tissue paper and method of producing tissue paper

A two-ply tissue paper having two outer side surfaces to which a chemical agent has been continuously applied, said chemical agent comprising from 70% to 90% polyol by weight and having a viscosity of from about 50 mPa·s to about 400 mPa·s at 40° C. at the time it is applied, said two-ply tissue paper further comprising:

• a chemical agent content for each one of said two side surfaces of from 3.0 to 5.0 g/m2;
• a weight per each ply constituting the two-ply tissue paper including said chemical agent of from 11 g/m2 to 16 g/m2;
• a sheet thickness for said two-ply tissue paper of from 100 um to 140 um;
• and a coefficient of static friction of the two-ply tissue is 0.55 to 0.65, wherein said coefficient of static friction is measured by following step (A) to (D):
• (A) a segment of the two ply tissue paper is separated into two single ply sheets of tissue paper and the one of said single-ply sheets of tissue paper is attached to an acrylic plate so that the surface of said single-ply sheet of tissue paper that had been an outer side surface of said two ply tissue paper faces outside;
• (B) a second segment of the two ply tissue paper is wound on a weight of 100 g while a two ply structure is maintained and the weight is placed on the one ply tissue paper attached to the acrylic plate;
• (C) an angle at which the weight slides and falls is measured by inclining the acrylic plate;
• and (D) the angle is measured eight times in total, four times between MD direction of the one ply tissue paper and MD direction of the two ply tissue paper and four times between CD direction of the one ply tissue paper and CD direction of the two ply tissue paper so that an average angle is calculated, and a tangent value thereof is set as the static friction coefficient, and said two-ply tissue paper is a blowing nose tissue paper contained within a box for storage and retrieval of said tissue paper.