A method for producing a metal containing composite, comprising:
- a step of preparing an adhesive (B) containing solvent and formed as a suspension of low viscosity by adding a ketone solvent to a one-part epoxy adhesive (A) using dicyandiamide as a curing agent and mixing the same;
- a step of preparing one kind of metal shaped article as an adherend selected from the following five kinds of metal shaped articles (M1 to M5):
- a metal shaped article (M1), which, through surface treatment including chemical etching and/or surface hardening, has a surface with ultrafine irregularities covered entirely with substantially ultrafine bowl-shaped concaves of 20 to 100 nm diameter and in which said surface with said ultrafine irregularities is covered with a thin layer of ceramics comprising a metal oxide or a metal phosphate,
- a metal shaped article (M2), which, through surface treatment including chemical etching and/or surface hardening, has a roughened surface, in which a forest of convexes shaped like thick walls or convexes of indefinite shapes as formed by collapse of such thick walls with short dimension and long dimension of 0.05 to 1 μm and height of more than 0.3 μm stand with space of 0.1 to 2 μm therebetween, the roughened surface being entirely covered with ultrafine irregularities having period of 20 to 100 nm and the whole surface being covered with a thin layer of ceramics comprising a metal oxide or a metal phosphate,
- a metal shaped article (M3), which, through surface treatment including chemical etching and/or surface hardening, has a roughened surface having bowl-like concave faces of 1 to 5 μm period, the roughened surface being entirely covered with ultrafine irregularities having period of 20 to 100 nm and the whole surface being covered with a thin layer of ceramics comprising a metal oxide or a metal phosphate,
- a metal shaped article (M4), which, through surface treatment including chemical etching and/or surface hardening, has a surface with ultrafine irregularities covered entirely with cubic protrusions in a dimension of 10 to 200 nm or mixed protrusions of such cubic protrusions and disc-shaped protrusions of 100 to 250 nm diameter standing on a plain in a density of 5 to 50 per square of 200 nm side, the whole surface being covered with a thin layer of ceramics comprising a metal oxide or a metal phosphate, and
- a metal shaped article (M5), which, through surface treatment including chemical etching and/or surface hardening, has a surface configuration loaded with spherical entities of about 100 run diameter combined among themselves along with a configuration of numerous short whiskers below 10 nm growing on the surface of the spherical entities, the whole surface being covered with a thin layer of ceramics comprising a metal oxide or a metal phosphate;
- a step of painting a face for adhesion of said selected metal shaped article (M1 to M5) with said adhesive (B) containing solvent and volatilizing the ketone solvent in a drying machine or through air-drying;
- a step of preparing a resin shaped article (P1) as another adherend by curing a thermosetting epoxy resin composition comprising an epoxy resin as a main constituent;
- a step of forming a roughened face for adhesion of the resin shaped article (P1) with several decades μm order on a specified portion of said resin shaped article (P1) by grinding it with physical means, cleaning with water, drying and removing dirt;
- a step of painting the roughened face for adhesion of said resin shaped article (P1) with said adhesive (B) containing solvent and volatilizing the ketone solvent in a drying machine or through air-drying;
- and
- a step of causing the face for adhesion of said selected metal shaped article (M1 to M5) and the roughened face of adhesion of said resin shaped article (P1), both of which were painted with the one-part epoxy adhesive to abut on each other and fixing the metal shaped article and the resin shaped article, heating the fixed shaped articles at a temperature of 150 to 180° C. and curing the one-part adhesive to accomplish adhesion,
- wherein the tensile strength of adhesion between the metal shaped article and the resin shaped article is equal to or higher than the shear strength of adhesion.