# US 9,873,185 B2 · Rapid curing of resin bonded grinding wheels > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 9,873,185 B2 - Document ID: US9873185B2 - Status: Granted - Kind: B2 - Application number: 14/415,074 - Filed: 2013-07-17 - Published: 2015-06-18 - Granted: 2018-01-23 - Earliest claimed: 2012-07-19 - Assignees: Pradeep Metals Limited - Applicants: Pradeep Metals Limited - Inventors: Pradeep Goyal; Shivanand Borkar; Ritesh Jaiswal - Web page: https://patentgrep.com/patent/US9873185B2 ## CPC - B24D 18/0072: {using adhesives for bonding abrasive particles or grinding elements to a support, e.g. by gluing} - B24D 3/28: Resins {or natural or synthetic macromolecular compounds (B24D3/22 takes precedence)} - B24D 18/00: Manufacture of grinding tools {or other grinding devices}, e.g. wheels, not otherwise provided for - H05B 6/645: {using temperature sensors} - B24D: TOOLS FOR GRINDING, BUFFING OR SHARPENING (abrading-bodies specially designed for tumbling apparatus, e.g. abrading-balls B24B31/14; honing tools B24B33/08; lapping tools B24B37/11) - H05B: ELECTRIC HEATING; ELECTRIC LIGHT SOURCES NOT OTHERWISE PROVIDED FOR; CIRCUIT ARRANGEMENTS FOR ELECTRIC LIGHT SOURCES, IN GENERAL ## Abstract A system and process for rapid and uniform curing of grinding wheels (2) to obtain grinding wheels (2) with better durability, at 180-220° C. deploying microwave energy at 800-5000 MHz in which closely fitting green wheel sample holders (1) are made of carbon bearing microwave susceptor materials such as graphite, silicon carbide with tiny holes on the surface. These sample holders (1) help in maintaining the shape and geometry of the final wheels (2) after curing and reduce energy consumption. The performance of the grinding wheels (2) cured by this process is better than those cured by presently used process employing steel plate sample holders of the present state-of-art. ## Claims ### Claim 1 A system for rapid and uniform curing of grinding wheels for obtaining grinding wheels, comprising a. a plurality of green samples of grinding wheels, b. a microwave cavity, c. a plurality of sample holders made from materials susceptible to microwaves at room temperature, each sample holder having a substantially identical profile as a corresponding one of the green samples of grinding wheels, d. a temperature sensor, and e. a temperature controller for controlling the temperature of the sample within the microwave cavity. ### Claim 2 (depends on 1) The system as claimed in claim 1, wherein the grinding wheels are resin bonded. ### Claim 3 (depends on 1) The system as claimed in claim 1, wherein the materials susceptible to microwaves are selected from carbon bearing material. ### Claim 4 (depends on 3) The system as claimed in claim 3, wherein the materials susceptible to microwaves are graphite. ### Claim 5 (depends on 3) The system as claimed in claim 3, wherein the sample holders have holes on a surface. ### Claim 6 (depends on 1) The system as claimed in claim 1, wherein the microwave cavity provides microwave radiations in the frequency range of 800-5000 MHz. ### Claim 7 (depends on 6) The system as claimed in claim 6, wherein the microwave cavity provides microwave radiations in the frequency range of 890-2450 MHz. ### Claim 8 (depends on 6) The system as claimed in claim 6, wherein the microwave cavity provides microwave radiations in the frequency range of 2450+/−50 MHz. ### Claim 9 (depends on 1) The system as claimed in claim 1, wherein the microwave cavity provides microwave radiations in either a continuous manner, a pulsed manner, or both. ### Claim 10 (depends on 1) The system as claimed in claim 1, wherein the temperature controller maintains a temperature in the range of 180-220° C. based on the shape, size and composition of the grinding wheel. ### Claim 11 A process for rapid and uniform curing of green grinding wheels for obtaining grinding wheels, comprising a. preparing a sample holder such that a green sample of a grinding wheel to be cured fits snugly in the sample holder, the sample holder made from materials susceptible to microwaves at room temperature; b. placing the green sample in the sample holder; c. placing the sample holder with the green sample in the microwave cavity; d. stacking one or more additional sample holders with additional green samples in them, if necessary; e. deploying microwave energy for a predetermined time to attain a desired temperature as required for at least partially curing the green samples; f. removing the sample holder(s) along with the cured grinding wheel(s) from the microwave cavity and separating the cured grinding wheels from the sample holder(s) for reuse. ### Claim 12 (depends on 11) The process as claimed in claim 11, wherein the green samples are of resin bonded grinding wheels. ### Claim 13 (depends on 11) The process as claimed in claim 11, wherein the sample holders are prepared from carbon bearing material. ### Claim 14 (depends on 13) The process as claimed in claim 13, wherein the sample holders are prepared from graphite. ### Claim 15 (depends on 13) The process as claimed in claim 13, wherein the sample holder(s) have holes on the surface. ### Claim 16 (depends on 11) The process as claimed in claim 11, wherein the microwave energy deployed is of 800-5000 MHz. ### Claim 17 (depends on 16) The process as claimed in claim 16, wherein the microwave energy deployed is of 890-2450 MHz. ### Claim 18 (depends on 16) The process as claimed in claim 16, wherein the microwave energy deployed is of 2450+/−50 MHz. ### Claim 19 (depends on 11) The process as claimed in claim 11, wherein the green samples of grinding wheels are heated in the microwave cavity in the range of 180-220° C. ### Claim 20 (depends on 19) The process as claimed in claim 19, wherein the green samples are heated in the microwave cavity at about 220° C. or less. ### Claim 21 (depends on 11) The process as claimed in claim 11, wherein the green sample is a depressed resinoid grinding wheel of 100 mm diameter, 5 mm thick and 15 mm hole diameter, weighing about 90 g and consisting of alumina grains mixed with phenolic resin and fillers, where the sample holder includes at least two about 12 mm thick graphite susceptors weighing about 200 g each and, where the sample is cured at about 220° C. in a 700 W microwave system for about 90 minutes to obtain a substantially uniformly cured depressed resinoid grinding wheel. ### Claim 22 (depends on 15) The process as claimed in claim 15, where the sample holder allows part of the microwaves to impinge directly on the green sample held in it.