Composite fibre components and the production thereof

A fiber composite component based on polyurethane, comprising one or more fiber layers each impregnated with polyurethane, wherein the polyurethane is obtained from a reaction mixture consisting of:

• A) one or more organic NCO prepolymers having an NCO content of 27% to 31% by weight and a monomer content of 35% to 55% by weight, wherein the NCO prepolymers comprise a reaction product of:
• aliphatic, cycloaliphatic, and/or aromatic di-isocyanates and/or polyisocyanates, and
• 5% to 7.5% by weight, based on component A), of condensation products which have ester groups, each condensation product having a number-average molecular weight of 650 to 3000 g/mol, an acid number of less than 5, a hydroxyl number of 28 to 112, and in each case a number-average functionality of 1.0 to 3.0, and wherein the condensation products are formed from:
• one or more fatty acids having 10 to 30 carbon atoms, one or more low molecular weight aliphatic and/or aromatic di-carboxylic and/or tricarboxylic acids each having number-average molecular weights of 50 to 500 g/mol, and/or derivatives thereof, and
• one or more mono-hydric or polyhydric alcohols each having a number-average molecular weight up to 500 g/mol and each having a number-average functionality of 1.5 to 6,
• B) a component comprising one or more polyols each having a number-average molecular weight of 62 to 3000 g/mol and each having a number-average functionality of 1.8 to 6,
• C) two or more thermolatent catalysts, and
• D) optionally additives,
• wherein component B) contains 2.5% to 3.5% by weight, based on component B), of an internal mold release agent, wherein the internal mold release agent comprises condensation products which have ester groups, each condensation product having a number-average molecular weight of 650 to 3000 g/mol, an acid number of less than 5, a hydroxyl number of 28 to 112, and a number-average functionality of 1.0 to 3.0, and wherein the condensation products are formed from:
• one or more fatty acids having 10 to 30 carbon atoms, one or more low molecular weight aliphatic and/or aromatic di-carboxylic and/or tricarboxylic acids each having a number-average molecular weight of 50 to 500 g/mol, and/or derivatives thereof, and
• one or more mono-hydric or polyhydric alcohols each having a number-average molecular weight up to 500 g/mol and each having a number-average functionality of 1.5 to 6,
• wherein the total amount of the condensation products having ester groups used in the fiber composite component is 5% to 5.7% by weight, and wherein the reaction mixture at 25° C. has a viscosity directly after the mixing of 200 to 700 mPas (measured according to DIN EN ISO 1342) and the ratio of the number of NCO groups of component A) to the number of OH groups of component B) is 1:1 to 1.15:1.