Catalyst for direct NOx decomposition and a method of forming and using the catalyst

Abstract

A process of forming a direct NOx catalyst includes the steps of providing a palladium salt, providing a silicon oxide support material, mixing the palladium salt and silicon oxide support material in an aqueous solution, evaporating the aqueous solution forming a solid, calcining the solid, and then exposing the calcined solid to a pretreatment gas at a specified temperature to form a desired direct NOx catalyst. When the process includes exposing the calcined solid to helium gas at a temperature of from 650 to 1000° C. the catalyst may include a mixture of palladium and palladium oxide having a particle size of from 5 to 150 nm where the palladium particles are discrete particles without sintering and the mixture may include 41% by weight palladium oxide and 51% by weight palladium metal.