Method for producing anti-blocking hard coat film

A method for producing a transparent hard coat film having a hard coat formed from an active energy ray-curable resin composition on at least one surface of a film base material, wherein the active energy ray-curable resin composition comprises:

• 100 parts by mass of (P) a urethane (meth)acrylate compound;
• 0.02 to 5 parts by mass of (Q) organic fine particles having an average particle size of 10 to 300 nm;
• and
• 0.0002 to 2 parts by mass of (R) an acrylic silicon leveling agent,
• the method comprising the steps of:
• (1) coating the film base material with the active energy ray-curable resin composition to form a wet coating film;
• (2) drying the wet coating film in a drying path set at a temperature of 40° C. or more to form a dry coating film;
• and
• (3) irradiating the dry coating film with an active energy ray at a temperature of 50 to 90° C. to cure the dry coating film to form the hard coat film,
• wherein the (R) acrylic silicon leveling agent is loaded in the active energy ray-curable resin composition in an amount of 1 part by mass or more based on 100 parts by mass of the (Q) organic fine particles.