Transparent conductive film and production method therefor

A transparent conductive film, comprising:

• an organic polymer film substrate;
• at least one undercoat layer formed on the organic polymer film substrate by a dry process;
• and
• a transparent conductive coating provided on at least one surface of the organic polymer film substrate with the undercoat layer interposed therebetween, wherein
• at least a portion of the at least one undercoat layer comprises inorganic material, wherein
• the transparent conductive coating is directly formed on the at least one undercoat layer, wherein
• the transparent conductive coating is a crystalline coating of an indium-based complex oxide having a content of a tetravalent metal element oxide of 7 to 15% by weight as calculated by the formula {(the amount of the tetravalent metal element oxide)/(the amount of the tetravalent metal element oxide+the amount of indium oxide)}×100(%), wherein
• the transparent conductive coating has a ratio (I440/I222) of the (440) peak intensity (I440) to the (222) peak intensity (I222) of less than 0.2;
• wherein
• the transparent conductive coating has a thickness in the range of 10 to 40 nm, and
• the transparent conductive coating has a specific resistance of 1.3×10−4 to 2.0×10−4 Ω·cm.