Low melting point braze alloy for high temperature applications
AssigneeSiemens Energy, Inc.
InventorsKazim Kazim, Sebastian Piegert
Life of this patent
Estimating the term…
Abstract
A multi component braze filler alloy is described having a melting temperature less than about 1235 deg. C. and greater than about 1150 deg. C. This alloy can be processed by hot isostatic pressing (HIP) at a temperature above about 1065 deg. C. and is particularly suited for the repair of gas turbine blades and vanes, especially those made from Alloy 247. The relatively low Ti content in the present braze alloy tends to form less MC carbides at the joint interface, particularly in comparison with other braze alloys high in Zr and/or Hf. Processes for employing this braze filler alloy in processing of nickel-base superalloys, especially Alloy 247, are presented.
Claims10
A method for repairing at least one crack in a nickel-base superalloy component comprising:
- a) applying to said at least one crack a quantity of a braze alloy having substantially the following composition in weight percents:
- Ni(XNi)—Cr(XCr)—Ti(XTi)—Al(XAl)—Co(XCo)—W(XW)—Mn(XMn)—Ta(XTa) wherein said weight percentages Xz lie in the following ranges:
- 12%≦XCr≦16%,
- 13%≦XTi≦16%,
- 0%<XAl≦2%,
- 2%≦XCo≦4%,
- 3%≦XW≦5%,
- 0%<XMn≦2%,
- 0%<XTa≦2%,
- XNi=(balance), and;
- b) brazing said nickel-base superalloy component having said braze alloy in said at least one crack at a brazing temperature in the range from approximately 1225 deg. C. to approximately 1250 deg. C., wherein said nickel-base superalloy is not substantially damaged at said brazing temperature.
A method for repairing at least one crack in a nickel-base superalloy component comprising:
- a) preparing a braze alloy having substantially the following composition in weight percents:
- Ni(XNi)—Cr(XCr)—Ti(XTi)—Al(XAl)—Co(XCo)—W(XW)—Mn(XMn)—Ta(XTa) wherein said weight percentages Xz lie in the following ranges:
- 12%≦XCr≦16%,
- 13%≦XTi≦16%,
- 0%<XAl≦2%,
- 2%≦XCo≦4%,
- 3%≦XW≦5%,
- 0%<XMn≦2%,
- 0%<XTa≦2%,
- XNi=(balance), and;
- b) mixing said braze alloy with a powder having substantially the same composition as said nickel-base superalloy component thereby preparing a braze mixture, and;
- c) applying said braze mixture to said at least one crack, and;
- d) brazing said component having said braze mixture in said at least one crack at a brazing temperature in the range from approximately 1225 deg. C. to approximately 1250 deg. C., wherein said nickel-base superalloy is not substantially damaged at said brazing temperature.
Dependencies are inferred from the claim text.