Zone melting furnace thermal field with dual power heating function and heat preservation method

A zone melting furnace heat preservation method on the basis of the zone melting furnace thermal field with the dual power heating function including a primary heating coil provided with a circular hole in a center and connected with a primary heating power supply, and an auxiliary heater which has a wavy appearance bent repeatedly up and down and forms a circular loop by surrounding in a horizontal direction, wherein both end parts of the auxiliary heater are provided with ports and are connected with an auxiliary heating power supply through cables, wherein a diameter of the circular loop is 150 mm-400 mm and a height of the wavy appearance bent repeatedly up and down is 50 mm-800 mm;

• the auxiliary heating power supply is also sequentially connected with a data analysis module and an infrared temperature measuring instrument through signal lines, the primary heating power supply and the auxiliary heating power supply are independent of each other, and each of the primary heating power supply and the auxiliary heating power supply is provided with a control operation module and a shielding anti-interference device, the method comprising:
• applying a direct current power supply to the auxiliary heater by means of the auxiliary heating power supply;
• applying thermal irradiation by the auxiliary heater to a single crystal rod growing therein, and thus realizing heat preservation to the single crystal rod;
• the infrared temperature measuring instrument is configured to monitor the temperature of a specific point of the single crystal rod in real time and transmit the temperature to the data analysis module, and the data analysis module is configured to control a current of the auxiliary heater by virtue of built-in control methods, so as to adjust a heat preservation effect on the single crystal rod;
• wherein the built-in control methods of the data analysis module include a control target that refers to the temperature of the specific point of the single crystal rod, a control input refers to the current of the auxiliary heater, and different control strategies are adopted in different growth stages, comprising:
• in a shoulder expanding stage, a diameter of the single crystal rod continuously changes, and a change curve T(d) of the temperature of the specific point of the single crystal rod along with the diameter of the single crystal rod is set as a target value, wherein the change curve T(d) of the temperature of the specific point of the single crystal rod along with the diameter of the single crystal rod is obtained in a manner of calibrating a production process of the single crystal rod as a standard reference;
• and when the diameter of the single crystal rod is D, the target value T(D) of the temperature of the single crystal rod is obtained through looking up the curve, and temperature deviation ΔT=T1−T(D), wherein T1 is the temperature, detected by the infrared temperature measuring instrument, of the specific point of the single crystal rod when the diameter of the single crystal rod is D;
• a current set value I of the auxiliary heater is controlled in three stages:
• when the temperature deviation ΔT<Tm, I=Imax, namely the auxiliary heater outputs a maximum current;
• when ΔT>Tb, I=0, namely the auxiliary heater is switched off;
• when Tm≦ΔT≦Tb, I=I0−0.45×ΔT+0.0038×(D/ΔT), wherein Tm is a lower deviation allowed when the target value of the temperature of the single crystal rod is T(D), Tb is an upper deviation allowed when the target value of the temperature of the single crystal rod is T(D), both of which meet −20° C.≦Tm≦0° C.≦Tb≦20° C., and I0 is an initial set value of the current of the auxiliary heater in the shoulder expanding stage and ranges from 0.3Imax to 0.5Imax;
• in an equal diameter stage, the current set value I of the auxiliary heater is I1+0.05×T, wherein I1 is an initial set value of the current of the auxiliary heater in the equal diameter stage and ranges from 0.4Imax to 0.7Imax, and T is time entering the equal diameter stage;
• in an ending stage, a change curve T(d)′ of the temperature of the specific point of the single crystal rod along with the diameter of the single crystal rod is set as a target value, wherein the change curve T(d)′ of the temperature of the specific point of the single crystal rod along with the diameter of the single crystal rod is obtained in a manner of calibrating the production process of the single crystal rod as a standard reference;
• and when the diameter of the single crystal rod is D, the target value T(D)′ of the temperature of the single crystal rod is obtained through looking up the curve, and temperature deviation ΔT=T1′−T(D)′, wherein the T1′ is the temperature, detected by the infrared temperature measuring instrument, of the specific point of the single crystal rod when the diameter of the single crystal rod is D;
• and
• a current set value I of the auxiliary heater is controlled in three stages:
• when the temperature deviation ΔT′<Tm′, I=Imax, namely the auxiliary heater outputs the maximum current;
• when ΔT′>Tb′, I=0, namely the auxiliary heater is switched off;
• when Tm′≦ΔT′≦Tb′, I=I0′−0.65×ΔT′+0.0025×(D/ΔT′), wherein Tm′ is a lower deviation allowed when the target value of the temperature of the single crystal rod is T(D)′, Tb′ is an upper deviation allowed when the target value of the temperature of the single crystal rod is T(D)′, both of which meet −20° C.≦Tm≦0° C.≦Tb≦20° C., and I0′ is an initial set value of the current of the auxiliary heater in the ending stage and ranges from 0.3Imax to 0.5Imax.