Basalt fibers produced from high temperature melt
AssigneeAmericas Basalt Technology, LLC
InventorsYevgeniy Zubko, Yurii Zubko
Life of this patent
Estimating the term…
Abstract
Methods, systems and apparatus for producing continuous basalt fibers, microfibers, and microspheres from high temperature melts are disclosed. A cold crucible induction furnace is used to super heat crushed basalt rock to form a melt. The melt is cooled prior to forming a fiber. The fiber produced from the superheated melt possesses superior properties not found with conventional basalt fibers produced in gas furnaces. In some implementations, the superheated melt is spun into continuous basalt fibers. In some implementations, the superheated melt is blown into microfibers and microspheres.
Claims18
A method of producing a continuous basalt fiber, comprising:
- charging a quantity of basalt into an induction furnace, the induction furnace having an interior comprising copper plates and containing substantially no refractory lining;
- inductively heating at least about 100 kilograms of basalt in the induction furnace to a first temperature of at least about 2500° C. to form a melt;
- cooling the melt to a temperature below 1500° C. by passing the melt through a water cooled tray to form a cooled melt;
- and
- forming the continuous basalt fiber from the cooled melt, wherein 1 kilogram of continuous basalt fiber is produced using less than 2.2 kilowatts of electrical power, and wherein the continuous basalt fiber is from about 1 microns to about 3 microns in diameter.
A method of producing a continuous fiber, comprising:
- charging a quantity of a rock in an induction furnace, the induction furnace having an interior comprising copper plates and containing substantially no refractory lining, the rock comprising plagioclase having a plagioclase melting point and a component having a component melting point, wherein the plagioclase melting point is less than the component melting point;
- inductively heating the quantity of the rock in the induction furnace to a furnace temperature above the component melting point to form a superheated melt, wherein the superheated melt is at least about 98% amorphous and the furnace temperature is at least about 2500° C.;
- cooling the superheated melt to a temperature between the plagioclase melting point and the component melting point by passing the superheated melt through a water cooled tray to form a cooled melt;
- and
- forming the continuous fiber from the cooled melt.
A method of producing a continuous basalt fiber, comprising:
- charging a quantity of basalt into a cold crucible induction furnace wherein the induction furnace has an interior comprising copper plates and containing substantially no refractory lining;
- inductively heating the quantity of the basalt in the cold crucible induction furnace to a temperature of at least about 2500° C. to form a homogenous melt, wherein the cold crucible induction furnace heats about 1 kilogram of basalt per less than 2.2 kilowatts of electrical power;
- cooling the homogenous melt to a temperature less than about 1500° C. by passing the melt through a water cooled tray to form a cooled homogenous melt;
- and
- forming the continuous basalt fiber by passing the cooled homogenous melt through a bushing.
A method of producing a continuous basalt fiber from a homogeneous melt, comprising:
- charging a quantity of basalt rock into a cold crucible induction furnace;
- inductively heating the quantity of the basalt in the cold crucible induction furnace to a temperature of at least about 2500° C. to form a homogenous melt having a viscosity of less than about 500 cP, wherein the cold crucible induction furnace includes an interior comprising copper plates and containing substantially no refractory lining;
- wherein the cold crucible induction furnace heats about 1 kilogram of basalt per less than 2.2 kilowatts of electrical power;
- cooling the homogenous melt to a temperature less than about 1500° C. by passing the homogenous melt through a water cooled tray;
- forming the continuous basalt fiber by passing the cooled homogenous melt through a bushing;
- applying a spin finish to the continuous basalt fiber.
Dependencies are inferred from the claim text.