# US 9,752,203 B2 · Process to improve fatigue strength of micro alloy steels, forged parts made from the process and an apparatus to execute the process > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 9,752,203 B2 - Document ID: US9752203B2 - Status: Granted - Kind: B2 - Application number: 14/350,082 - Filed: 2012-10-03 - Published: 2014-09-18 - Granted: 2017-09-05 - Earliest claimed: 2011-10-07 - Applicants: Babasaheb Neelkanth Kalyani - Inventors: Babasaheb Neelkanth Kalyani - Web page: https://patentgrep.com/patent/US9752203B2 ## CPC - C21D 1/18: Hardening (C21D1/02 takes precedence); Quenching with or without subsequent tempering (quenching devices C21D1/62) - C21D 1/02: Hardening articles or materials formed by forging or rolling, with no further heating beyond that required for the formation - C21D 1/42: Induction heating - C21D 7/13: by hot working - C21D 9/30: for crankshafts; for camshafts - F16C 3/06: Crankshafts - C21D 2211/001: Austenite - Y02P 10/25: Process efficiency - C21D: MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING (surface treatment of metallic material involving at least one process provided for in class C23 and at least one process covered by this subclass C23F17/00; unidirectional solidification of eutectic materials or unidirectional demixing of eutectoid materials C30B) - F16C: SHAFTS; FLEXIBLE SHAFTS; ELEMENTS OR CRANKSHAFT MECHANISMS; ROTARY BODIES OTHER THAN GEARING ELEMENTS; BEARINGS - Y02P: CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS ## Abstract The present invention describes a process to make enhanced fatigue strength micro-alloy steel. In the process of the present invention, the soaking temperature is maintained in the range of 900° C. to 1050° C. and soaking time in the range of 30-60 minutes depending on size of crankshaft to get refined grain size. Distortion of the components is prevented from occurring with provision of adequate supports especially designed for the process. Forged parts made using the process, such as crankshafts, have a refined grain pattern and result into 20 to 25% enhancement in torsion fatigue strength & 10-25% enhancement in bending fatigue strength. The present invention thus provides an enhanced ratio of the strength to material density and a micro-alloy whose torsion fatigue strength and bending fatigue strength are greater than the currently available micro-alloy steels. ## Claims ### Claim 1 A process to improve fatigue strength of forged parts made from vanadium micro alloy steels, said process having a step of refining the grain size, said step of refining the grain size in turn comprising: austenitising said parts by heating them to a first temperature which is in the range between 900-1050° C., maintaining said parts at that temperature for a soaking period in order to allow said part to attain homogenized temperature, and cooling said parts to room temperature. ### Claim 2 (depends on 1) A process as claimed in claim 1, wherein said soaking period is 30 to 60 minutes. ### Claim 3 (depends on 1) A process as claimed in claim 1, wherein said cooling is applied by still or forced air cooling methods. ### Claim 4 (depends on 3) A process as claimed in claim 3, wherein during the austenitising, soaking and cooling stages, warp-avoidance support is provided to each of said parts. ### Claim 5 A forged part made from vanadium micro alloy steels said part having improved grain size and structure, obtained through a process of forging that comprises a step of improving grain size, said improved grain structure being a pearlite structure, said improved grain size being between ASTM 6-8, and said step comprising: austenitising said parts by heating them to a first temperature which is in the range between 900-1050° C., maintaining said parts at that temperature for a soaking period in order to allow said part to attain homogenized temperature, and cooling said parts to room temperature. ### Claim 6 (depends on 5) A forged part as claimed in claim 5, wherein said soaking period is 30 to 60 minutes. ### Claim 7 (depends on 5) A forged part as claimed in claim 5, wherein said cooling is applied by still or forced air cooling methods. ### Claim 8 (depends on 7) A forged part as claimed in claim 7, wherein during the austenitising, soaking and cooling stages, warp-avoidance support is provided to each of said parts. ### Claim 9 An apparatus to make a forged part from vanadium micro alloy steels, said apparatus comprising at least a grain size refinement station wherein steps of austenitising, soaking and cooling of said forged part are carried out. ### Claim 10 A process to improve fatigue strength of forged parts made from vanadium micro alloy steels, said process having a step of refining the grain size, said step of refining the grain size in turn comprising: austenitising said parts by heating them to a first temperature which is in the range between 900-1050° C., maintaining said parts at that temperature for a soaking period in order to allow said part to attain homogenized temperature, and cooling said parts to room temperature, wherein said soaking period is 30 to 60 minutes, and wherein said cooling is applied by still or forced air cooling methods. ### Claim 11 (depends on 10) A process as claimed in claim 10, wherein during the austenitising, soaking and cooling stages, warp-avoidance support is provided to each of said parts.