Composite system
OwnerRobert G. Leeinventor
Life of this patent
Estimating the term…
Abstract
A multiphase composite system is made by binding hard particles, such as TiC particles, of various sizes with a mixture of titanium powder and aluminum, nickel, and titanium in a master alloy or as elemental materials to produce a composite system that has advantageous energy absorbing characteristics. The multiple phases of this composite system include an aggregate phase of hard particles bound with a matrix phase. The matrix phase has at least two phases with varying amounts of aluminum, nickel, and titanium. The matrix phase forms a bond with the hard particles and has varying degrees of hard and ductile phases. The composite system may be used alone or bonded to other materials such as bodies of titanium or ceramic in the manufacture of ballistic armor tiles.
Claims28
A mixture of materials to be used in the production of a green compact for sintering comprising:
- a) 12.5 wt. % to 25 wt. % of a powder comprising
- 24 wt % to 28 wt. % titanium
- 7 wt. % to 12 wt. % aluminum
- 0 wt. % to 0.10 wt. % carbon
- 0 wt. % to 4.5 wt. % iron
- 0 wt. % to 4 wt. % silicon
- with the balance being nickel and trace elements;
- and
- b) 32 wt % to 55 wt % of a hard powder,
- with the balance being titanium powder.
A green compact comprising:
- a) 12.5 wt. % to 25 wt. % of a powder comprising
- 24 wt % to 28 wt. % titanium
- 7 wt. % to 12 wt. % aluminum
- 0 wt. % to 0.10wt. % carbon
- 0 wt. % to 4.5 wt. % iron
- 0 wt. % to 4 wt. % silicon
- with the balance being nickel and trace elements,
- b) 32 wt % to 55 wt % of a hard powder, and
- c) titanium powder in an amount sufficient to impart sufficient green strength to the green compact.