# US 9,517,455 B2 · Catalyzed SCR filter and emission treatment system

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 9,517,455 B2
- Document ID: US9517455B2
- Status: Granted
- Kind: B2
- Application number: 14/454,931
- Filed: 2014-08-08
- Published: 2014-11-27
- Granted: 2016-12-13
- Earliest claimed: 2003-08-05
- Assignees: BASF SE
- Applicants: BASF Corporation
- Inventors: Joseph A. Patchett; Joseph C. Dettling; Elizabeth A. Przybylski
- Web page: https://patentgrep.com/patent/US9517455B2

## CPC

- B01J 29/7615: {Zeolite Beta}
- B01D 5/0054: {General arrangements, e.g. flow sheets}
- B01D 5/009: {Collecting, removing and/or treatment of the condensate}
- B01D 19/0005: {with one or more auxiliary substances}
- B01D 19/0036: {Flash degasification (the other groups take precedence)}
- B01D 53/9413: {Processes characterised by a specific catalyst}
- B01D 53/9418: {for removing nitrogen oxides by selective catalytic reduction [SCR] using a reducing agent in a lean exhaust gas}
- B01D 53/945: {characterised by a specific catalyst}
- B01D 53/9477: {with catalysts positioned on separate bricks, e.g. exhaust systems}
- B01J 29/76: Iron group metals or copper
- B01J 35/657: {larger than 1000 nm}
- B01J 37/0236: {Drying, e.g. preparing a suspension, adding a soluble salt and drying}
- B01J 37/024: {Multiple impregnation or coating}
- B01J 37/0246: {Coatings comprising a zeolite}
- B01J 37/08: Heat treatment {(B01J37/0009, B01J37/0018 take precedence)}
- F01N 3/0231: {using special exhaust apparatus upstream of the filter for producing nitrogen dioxide, e.g. for continuous filter regeneration systems [CRT]}
- F01N 3/10: by thermal or catalytic conversion of noxious components of exhaust
- F01N 3/106: {Auxiliary oxidation catalysts}
- F01N 3/2066: {Selective catalytic reduction [SCR]}
- F01N 3/2828: {Ceramic multi-channel monoliths, e.g. honeycombs}
- F01N 3/2892: {Exhaust flow directors or the like, e.g. upstream of catalytic device}
- F01N 13/009: {having two or more separate purifying devices arranged in series}
- B01D 53/944: {Simultaneously removing carbon monoxide, hydrocarbons or carbon making use of oxidation catalysts (three-way-catalysts [TWC] B01D53/9445)}
- B01D 2251/2062: Ammonia
- B01D 2251/2067: Urea
- B01D 2255/102: Platinum group metals
- B01D 2255/20715: Zirconium
- B01D 2255/20738: Iron
- B01D 2255/20761: Copper
- B01D 2255/50: Zeolites
- B01D 2255/502: Beta zeolites
- B01D 2255/9155: Wall flow filters
- B01D 2255/9202: Linear dimensions
- B01D 2255/9205: Porosity
- B01D 2257/404: Nitrogen oxides other than dinitrogen oxide
- B01D 2258/012: Diesel engines and lean burn gasoline engines
- B01J 35/56: Foraminous structures having flow-through passages or channels, e.g. grids or three-dimensional [3D] monoliths
- F01N 2330/06: Ceramic, e.g. monoliths
- F01N 2330/30: Honeycomb supports characterised by their structural details
- F01N 2370/04: Zeolitic material
- F01N 2510/063: zeolites
- F01N 2610/02: the substance being ammonia or urea
- F01N 2610/08: with prior mixing of the substances with a gas, e.g. air
- Y02T 10/12: Improving ICE efficiencies
- Y10S 55/10: Residue burned
- Y10S 55/30: Exhaust treatment
- Y10T 29/49345: Catalytic device making
- B01J: CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01D: SEPARATION (separating solids from solids by wet methods B03B, B03D; by pneumatic jigs or tables B03B; by other dry methods B07; magnetic or electrostatic separation of solid materials from solid materials or fluids, separation by high-voltage electric fields B03C; centrifuges, vortex apparatus B04; presses per se for squeezing-out liquid from liquid-containing material B30B9/02; treatment of water C02F, e.g. softening by ion-exchange C02F1/42; {arrangements of air intake cleaners in gas turbine plants F02C7/05} ; arrangements or mounting of filters in air-conditioning, air-humidification or ventilation F24F13/28)
- F01N: GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR MACHINES OR ENGINES IN GENERAL; GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR INTERNAL-COMBUSTION ENGINES (arrangements in connection with gas exhaust of propulsion units in vehicles B60K13/00; combustion-air intake silencers specially adapted for, or arranged on, internal-combustion engines F02M35/00; protecting against, or damping, noise in general G10K11/16)
- Y02T: CLIMATE CHANGE MITIGATION TECHNOLOGIES RELATED TO TRANSPORTATION
- Y10S: TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10T: TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION

## Abstract

Provided is a catalyst article for simultaneously remediating the nitrogen oxides (NOx), particulate matter, and gaseous hydrocarbons present in diesel engine exhaust streams. The catalyst article has a soot filter coated with a material effective in the Selective Catalytic Reduction (SCR) of NOx by a reductant, e.g., ammonia.

## Claims

### Claim 1

A catalyst article consisting essentially of a wall flow monolith and a catalytic material,
wherein the wall flow monolith has a plurality of longitudinally extending passages formed by longitudinally extending walls bounding and defining said passages, wherein the passages comprise inlet passages having an open inlet end and a closed outlet end, and outlet passages having a closed inlet end and an open outlet end, the wall flow monolith has a porosity of from 50% to 60% and an average pore size of from 10 to 25 microns, and the wall flow monolith contains the catalytic material;
wherein the catalytic material comprises an SCR catalyst composition including a slurry-loaded washcoat of a zeolite and base metal selected from one or more of a copper and iron component, the washcoat permeating the walls at a loading up to 2.4 g/in3, the wall flow monolith having integrated, NOx and particulate removal efficiency in which presence of the catalytic material in the wall flow monolith catalyzes the oxidation of soot.

### Claim 2 (depends on 1)

The catalyst article of claim 1, wherein the SCR catalyst composition permeates the walls of the monolith at a concentration of at least 1.3 g/in3.

### Claim 3 (depends on 2)

The catalyst article of claim 2, wherein there is from 1.6 to 2.4 g/in3 of SCR catalyst composition disposed on the wall flow monolith.

### Claim 4 (depends on 1)

The catalyst article of claim 1, wherein the SCR catalyst composition is effective to catalyze the reduction of NOx at a temperature below about 600° C. and is able to aid in regeneration of the wall flow monolith by lowering the temperature at which soot captured by the wall flow monolith is combusted.

### Claim 5 (depends on 1)

The catalyst article of claim 1, wherein the SCR catalyst composition has a thermal resistance to degradation at temperatures greater than 650° C.

### Claim 6 (depends on 5)

The catalyst article of claim 5, wherein the SCR catalyst composition is effective to resist degradation upon exposure to sulfur components.

### Claim 7 (depends on 1)

The catalyst article of claim 1, wherein the SCR catalyst composition promotes the oxidation of excess NH3 with O2.

### Claim 8 (depends on 1)

The catalyst article of claim 1, wherein the base metal component is a copper component and the zeolite of the SCR catalyst composition has a silica to alumina ratio of at least about 10.

### Claim 9 (depends on 8)

The catalyst article of claim 8, wherein the zeolite of the SCR catalyst composition is selected from beta zeolite, USY and ZSM-20.

### Claim 10 (depends on 8)

The catalyst article of claim 8, wherein the zeolite of the SCR catalyst composition is a beta zeolite.

### Claim 11 (depends on 8)

The catalyst article of claim 8, wherein the zeolite of the SCR catalyst composition has pores with a pore diameter of at least about 7 Angstroms and are connected in three dimensions.

### Claim 12 (depends on 1)

The catalyst article of claim 1, wherein the SCR catalyst composition contains one or both of an iron and a copper promoter present in an amount of from about 0.1 to 30 percent by weight of the total weight of promoter plus zeolite.

### Claim 13 (depends on 1)

The catalyst article of claim 1, wherein the SCR catalyst composition contains one or both of an iron and a copper promoter present in an amount of from about 1 to 5 percent by weight of the total weight of promoter plus zeolite.

### Claim 14 (depends on 1)

The catalyst article of claim 1, wherein the wall flow monolith has a wall porosity of from 55% to 60% with an average pore size of from 10 to 25 microns.

### Claim 15 (depends on 1)

The catalyst article of claim 1, wherein the longitudinally extending walls have an inlet side and an opposing outlet side and SCR catalyst is coated on both the inlet and outlet sides of the walls.

### Claim 16

A catalyst article consisting essentially of a wall flow monolith and a catalytic material,
wherein the wall flow monolith has a plurality of longitudinally extending passages formed by longitudinally extending walls bounding and defining said passages, wherein the passages comprise inlet passages having an open inlet end and a closed outlet end, and outlet passages having a closed inlet end and an open outlet end, the wall flow monolith has a porosity of from 50% to 60% and an average pore size of from 10 to 25 microns, and the wall flow monolith contains the catalytic material;
wherein the catalytic material comprises an SCR catalyst composition including a slurry-loaded washcoat of a zeolite and base metal selected from one or more of a copper and iron component, the washcoat permeating the walls at a loading up to 1.3 g/in3,
the wall flow monolith having integrated, NOx and particulate removal efficiency in which presence of the catalytic material in the wall flow monolith catalyzes the oxidation of soot.

### Claim 17 (depends on 16)

The catalyst article of claim 16, wherein there is from 1.6 to 2.4 g/in3 of SCR catalyst composition disposed on the wall flow monolith.

### Claim 18 (depends on 16)

The catalyst article of claim 16, wherein the SCR catalyst composition contains one or both of an iron and a copper promoter present in an amount of from about 0.1 to 30 percent by weight of the total weight of promoter plus zeolite.

### Claim 19 (depends on 16)

The catalyst article of claim 16, wherein the SCR catalyst composition has a thermal resistance to degradation at temperatures greater than 650° C.

### Claim 20

A catalyst article consisting essentially of a wall flow monolith and a catalytic material,
wherein the wall flow monolith has a plurality of longitudinally extending passages formed by longitudinally extending walls bounding and defining said passages, wherein the passages comprise inlet passages having an open inlet end and a closed outlet end, and outlet passages having a closed inlet end and an open outlet end, the wall flow monolith has a porosity of from 50% to 55% and an average pore size of from 10 to 25 microns, and the wall flow monolith contains the catalytic material;
wherein the catalytic material comprises an SCR catalyst composition including a slurry-loaded washcoat of a zeolite and base metal, the washcoat permeating the walls,
the wall flow monolith having integrated, NOx and particulate removal efficiency in which presence of the catalytic material in the wall flow monolith catalyzes the oxidation of soot.