Electrically conductive film

An electrically conductive film obtained by forming a metal layer having a regular mesh-like structure or an irregular random mesh-like structure on a resin substrate that is able to undergo elastic deformation,

• the stress relaxation rate (R) and the residual strain rate (α), as measured in a extension-restoration test described below, satisfy the following relationships:
• 20%≦R≦95% and
• 0%≦α≦3%;
• wherein in the extension-restoration test a piece of the electrically conductive film having a thickness of 50 μm and a shape of No. 6 dumbbell having a width of measured portion of 4 mm and a length of linear portion of 25 mm being subjected to an extension process and then a restoration process under the conditions described below using a tensile-compression tester in accordance with ISO 3384, and the stress relaxation rate (R) and the residual strain rate (α) being calculated using the calculation methods described below,
• Extension process conditions:
• deflection correction is carried out at a force of 0.05 N or lower,
• Speed of testing:
• 25 mm/min at 0 to 25% extension;
• Temperature conditions:
• 23° C.;
• Extension/holding conditions:
• holding for 5 minutes at 25% extension;
• Restoration process conditions:
• Speed of testing:
• 0.1 mm/min until the tensile force reaches 0±0.05 N;
• Temperature conditions:
• 23° C.;
• Stress relaxation rate calculation method:
• the tensile force being measured at the point when the extension process is complete, and this being defined as the initial tensile force (FA0), then the amount of strain being maintained for 5 minutes under the extension/holding conditions, after which the tensile force is measured, and this being defined as FA(t5), with the stress relaxation rate (R) being calculated using the following formula:
• R
• =
• F
• A
• ⁢
• ⁢
• O
• -
• F
• A
• ⁡
• (
• t
• ⁢
• ⁢
• 5
• )
• F
• AO
• ×
• 100
• ;
• Residual strain rate calculation method:
• the amount of strain being measured at the point where the tensile force in the restoration process reaches 0±0.05 N, and this being defined as the residual strain rate (α).