Fouling reduction in hydrochlorosilane production
AssigneeREC Silicon Inc
InventorsStein Julsrud, Anja Olafsen Sjastad
Life of this patent
Estimating the term…
Abstract
Embodiments of a method for reducing iron silicide and/or iron phosphide fouling and/or corrosion in a hydrochlorosilane production plant are disclosed. Sufficient trichlorosilane is included in a silicon tetrachloride process stream to minimize hydrogen chloride formation, thereby inhibiting iron (II) chloride formation and reducing iron silicide and/or iron phosphide fouling, superheater corrosion, or a combination thereof.
Claims19
A method for reducing fouling of a hydrogenation reactor in a hydrochlorosilane production plant comprising a silicon tetrachloride superheater having iron-containing walls and a hydrogenation reactor, the method comprising:
- including at least 0.2 mol % of trichlorosilane in a silicon tetrachloride process stream comprising silicon tetrachloride and hydrogen in the silicon tetrachloride superheater having iron-containing walls, so as to inhibit HCl formation in the silicon tetrachloride superheater when operating at a temperature sufficient to cause a reaction between the silicon tetrachloride and the hydrogen to produce HCl in the absence of the at least 0.2 mol % of trichlorosilane, thereby inhibiting FeCl2 formation by a reaction of HCl and iron in the iron-containing walls and transport of the FeCl2 to the hydrogenation reactor, and thereby reducing iron silicide fouling of the hydrogenation reactor by inhibiting iron silicide formation by a reaction of the silicon tetrachloride, hydrogen, and the FeCl2 that would be formed in the absence of the at least 0.2 mol % of trichlorosilane.
A method for inhibiting, during hydrochlorosilane production, corrosion of a silicon tetrachloride superheater in a hydrochlorosilane production plant comprising a silicon tetrachloride superheater having iron-containing walls and a hydrogenation reactor thereby reducing fouling of the hydrogenation reactor, the method comprising:
- including from 0.2 mol % to 2 mol % of trichlorosilane in a process stream of the silicon tetrachloride superheater, the process stream comprising silicon tetrachloride and hydrogen,
- wherein presence of the trichlorosilane in the process stream inhibits reaction of the silicon tetrachloride with the hydrogen at an operating temperature of the superheater thereby avoiding formation of HCl,
- further wherein avoiding the formation of the HCl inhibits a corrosive reaction of HCl with the iron-containing walls of the superheater, in turn reducing formation of FeCl2 and transport of the FeCl2 to the hydrogenation reactor, and
- further wherein reducing the formation of FeCl2 and transport of the FeCl2 to the hydrogenation reactor reduces iron silicide formation and associated iron silicide fouling of the hydrogenation reactor compared to iron silicide fouling produced by a process stream that does not comprise trichlorosilane.
A method for reducing fouling of a hydrogenation reactor in a hydrochlorosilane production plant comprising a silicon tetrachloride superheater having iron-containing walls and a hydrogenation reactor, the method comprising:
- including at least 0.2 mol % of trichlorosilane in a silicon tetrachloride process stream comprising silicon tetrachloride and hydrogen;
- flowing the silicon tetrachloride process stream comprising the at least 0.2 mol % of trichlorosilane into the silicon tetrachloride superheater having iron-containing walls;
- heating the silicon tetrachloride process stream comprising the at least 0.2 mol % of trichlorosilane in the silicon tetrachloride superheater to form a heated silicon tetrachloride process stream;
- and
- subsequently flowing the heated silicon tetrachloride process stream into the hydrogenation reactor, wherein the heated silicon tetrachloride process stream is mixed with a hydrogen process stream.
Dependencies are inferred from the claim text.