# US 9,436,138 B2 · Electrophotographic image forming fixing member, method for manufacturing said fixing member, and electrophotographic image forming apparatus

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 9,436,138 B2
- Document ID: US9436138B2
- Status: Granted
- Kind: B2
- Application number: 14/987,623
- Filed: 2016-01-04
- Published: 2016-07-07
- Granted: 2016-09-06
- Earliest claimed: 2015-01-06
- Assignees: Canon Kabushiki Kaisha
- Applicants: Canon Kabushiki Kaisha
- Inventors: Katsuhisa Matsunaka; Katsuya Abe; Naoki Akiyama; Yasuhiro Miyahara
- Web page: https://patentgrep.com/patent/US9436138B2

## CPC

- G03G 15/2057: {relating to the chemical composition of the heat element and layers thereof}
- G03G 2215/0135: the linear arrangement being vertical
- G03G 2215/2035: the fixing nip having a stationary belt support member opposing a pressure member
- G03G: ELECTROGRAPHY; ELECTROPHOTOGRAPHY; MAGNETOGRAPHY

## Abstract

A fixing member includes a substrate and an elastic layer on the substrate. The elastic layer comprises a cured product of a silicone rubber composition containing an anatase titanium oxide particle and an addition-curable silicone rubber, and undergoes cohesive failure in 90° peel test specified in JIS K6854-1: 1999. In the fixing member, an allyl group bound to a silicon atom is present at the interface between the substrate and the elastic layer.

## Claims

### Claim 1

A fixing member comprising:
a substrate; and
an elastic layer on the substrate, the elastic layer comprising a cured product of a silicone rubber composition containing a titanium oxide particle having an anatase crystal structure and an addition-curable silicone rubber,
wherein the elastic layer undergoes cohesive failure in a 90° peel test specified in JIS K6854-1:1999, and wherein an allyl group bound to an silicon atom is present at the interface between the substrate and the elastic layer.

### Claim 2 (depends on 1)

The fixing member according to claim 1, wherein when the substrate and the elastic layer are forcibly peeled from each other and the peeled surfaces are subjected to infrared spectroscopy by an attenuated total reflection method, at least one of infrared absorption spectra of the peeled surfaces of the substrate and the elastic layer has an absorption peak in the range of wavenumbers of 1630 cm−1 to 1640 cm−1.

### Claim 3 (depends on 1)

The fixing member according to claim 1, wherein the allyl group derives from a silane coupling agent containing an allyl group bound to a silicon atom.

### Claim 4 (depends on 1)

The fixing member according to claim 1, wherein the elastic layer has a tensile strength specified in JIS K6251: 2010 of 0.4 MPa or more and 3.0 MPa or less.

### Claim 5

A method for manufacturing a fixing member including a substrate, and an elastic layer on the substrate that is a cured product of a silicone rubber composition comprising a titanium oxide particle having an anatase crystal structure and an addition-curable silicone rubber, and that undergoes cohesive failure in 90° peel test specified in JIS K6854-1:1999, wherein an allyl group bound to a silicon atom is present at the interface between the substrate and the elastic layer, the method comprising the steps of:
applying a primer containing a silane coupling agent having an allyl group bound to a silicon atom onto a substrate;
baking the primer at a temperature of 50° C. or more and 120° C. or less;
forming a layer of a silicone rubber composition on the substrate after baking the primer, the silicone rubber composition containing a titanium oxide particle having an anatase crystal structure and an addition-curable silicone rubber; and
curing the silicone rubber in the layer.

### Claim 6 (depends on 5)

The method according to claim 5, wherein the silane coupling agent contains an organic silicon compound expressed by the following formula (1) or a condensate thereof:
CH2═CH—CH2—Si(—CH3)n(—OR)3-n (1),
wherein ‘OR’ is selected from the group consisting of alkoxy and carboxy, and n represents an integer of 1 to 3.

### Claim 7 (depends on 6)

The method according to claim 6, wherein ‘OR’ in the formula (1) is methoxy or ethoxy.

### Claim 8

An image forming apparatus comprising:
a fixing device configured to fix an unfixed toner image formed on a recording medium to the recording medium by heating and pressing, the fixing device including a fixing member,
wherein the fixing member includes a substrate, and an elastic layer on the substrate, the elastic layer comprising a cured product of a silicone rubber composition containing an anatase titanium oxide particle and an addition-curable silicone rubber,
wherein the elastic layer undergoes cohesive failure in 90° peel test specified in JIS K6854-1:1999, and
wherein an allyl group bound to a silicon atom is present at the interface between the substrate and the elastic layer.