# US 9,434,842 B2 · Mix composition determination method of coarse graded high modulus asphalt concrete with skeleton embedded structure

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 9,434,842 B2
- Document ID: US9434842B2
- Status: Granted
- Kind: B2
- Application number: 14/348,867
- Filed: 2012-10-16
- Published: 2014-09-04
- Granted: 2016-09-06
- Earliest claimed: 2011-10-17
- Assignees: Research Institute of Highway, Mot, Prc; Guangxi Communications Investment Group Co., Ltd.; Beijing Municipal Road & Bridge Building Material Group Co., Ltd.
- Applicants: Research Institute of Highway, Mot, Prc; Guangxi Communications Investment Group Co., Ltd; Beijing Municipal Road & Bridge Building Material Group Co., Ltd
- Inventors: Xudong Wang; Qin Fu; Xingye Zhou; Zhijie Chen; Lei Zhang; Hao Liu; Chaoyang Guo; Qian Xiao
- Web page: https://patentgrep.com/patent/US9434842B2

## CPC

- C08L 95/00: Compositions of bituminous materials, e.g. asphalt, tar, pitch
- C04B 26/26: Bituminous materials, e.g. tar, pitch {(C08L95/00 takes precedence)}
- C04B 2111/0075: {for road construction}
- C08L 2555/10: Design or test methods for bitumen or asphalt mixtures, e.g. series of measures, procedures or tests to obtain a bitumen or asphalt mixture having preset defined properties, general or international test methods, procedures or standards
- C08L: COMPOSITIONS OF MACROMOLECULAR COMPOUNDS (compositions based on polymerisable monomers C08F, C08G; artificial filaments or fibres D01F; textile treating compositions D06)
- C04B: LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE {(roofing granules E04D7/005)}; CERAMICS (devitrified glass-ceramics C03C10/00); REFRACTORIES; TREATMENT OF NATURAL STONE

## Abstract

The invention relates to mix composition determination method of coarse graded high modulus asphalt concrete with skeleton embedded structure, which belongs to the road engineering design field. The invention use low labeled hard asphalt AH-30# with penetration degree no greater than 30 (0.1 mm); the nominal maximum aggregate size no smaller than 26.5 mm; building mineral aggregate gradation of the mix using course aggregate gap gradation; using gradation design method of asphalt mixture based on closest compact condition to select the optimal oil-stone ratio.

## Claims

### Claim 1

A mix composition determination method for coarse graded high modulus asphalt concrete with a skeleton embedded structure, the method comprising:
first, determining a design grading curve of the coarse graded high modulus asphalt concrete with a skeleton embedded structure, based on calculating a passing rate value of each key mesh of an aggregate;
second, determining an optimal oil-stone ratio of asphalt concrete, such that the asphalt concrete provides a good performance, wherein the method further comprising:
choosing a low labeled hard asphalt with a penetration degree of no higher than 30 as a cementing material;
choosing a coarse aggregate, a fine aggregate and a mineral powder, wherein a maximum nominal size of the coarse aggregate is no smaller than 26.5 mm;
choosing the maximum nominal size of the coarse aggregates and corresponding key meshes;
determining the maximum nominal size of the coarse graded asphalt, an aggregate passing rate of three key meshes;
using passing rate of the maximum nominal size and a mesh size di to construct a first formula, and using passing rate of 4.75 mm and its mesh size to construct a second formula, and using the first formula and the second formula to calculate a coefficient A and a coefficient B from Pdi=A(di)B;
calculating the coefficient A and the coefficient B from Pdi=A(di)B using an aggregate passing rate, Pdi, of meshes having diameters, di, including the maximum nominal size and 4.75 mm;
using passing rate of the maximum nominal size and a mesh size di to construct a first formula, and using passing rate of 0.075 mm and its mesh size to construct a second formula, and using the first formula and the second formula to calculate a coefficient C and a coefficient D from Pdj.=C(dj)D;
calculating the coefficient C and the coefficient D from Pdj.=C(dj)D using an aggregate passing rate, Pdj, of meshes having diameters, dj, including diameters of 4.75 mm and 0.075 mm;
choosing 5-6 oil-stone ratios that interval is 0.3%-0.4% according to the design grading curve;
forming 4-6 specimens under each oil-stone ratio;
determining a gross volume density and a theoretical maximum density of the specimens;
calculating a dry density of the mix, voids in mineral aggregate (VMA) and voids in coarse aggregate (VCA);
drawing a quadratic curve between the dry density of the mix, the VMA, the VCA and the oil-stone ratio;
selecting an average of a first oil-stone ratio (OAC1) that corresponds to the minimum value of the VMA, a second oil-stone ratio (OAC2) that corresponds to the minimum value of the VCA and a third oil-stone ratio (OAC3) that corresponds to the maximum value of dry density of the mix;
determining an optimum oil-stone ratio OAC of coarse graded high modulus asphalt concrete with skeleton embedded structure from the following:
OAC=(OAC1+OAC2+OAC3)/3; and
preparing coarse graded high modulus asphalt concrete having the optimum oil-stone ratio OAC.

### Claim 2 (depends on 1)

The method according to claim 1, wherein the low labeled hard asphalt has a penetration degree of 30.

### Claim 3 (depends on 1)

The method according to claim 1, wherein the maximum nominal size of coarse aggregate is 26.5 mm.

### Claim 4 (depends on 1)

The method according to claim 1, wherein the gross volume density of the specimen is measured by wax sealing method.

### Claim 5 (depends on 1)

The method according to claim 1, wherein the theoretical maximum density of the specimen is measured by vacuum method.

### Claim 6 (depends on 1)

The method of claim 1, wherein choosing the maximum nominal size of coarse aggregates and corresponding key meshes further comprises choosing the maximum nominal size of the asphalt mixture, the 4.75 mm and the 0.075 mm aggregate, followed by giving an expected passing rate value of each key meshes.