Hand-held conformable sanding block
AssigneeTrade Associates, Inc.
InventorBang Fang Lin
Life of this patent
Estimating the term…
Abstract
An elastomeric sanding block conformable to curved or flat surfaces includes a Shore A hardness ranging from about 30 to about 90, and is made from ethylene-vinyl acetate copolymer, low-density polyethylene or an admixture thereof. The polymer or admixture ranges from about 35 to about 70 percent of the sanding block composition by weight. A blowing agent is present in an amount that ranges from about 1.5 to about 4.5 percent of the composition by weight. The elastomeric sanding block may be formed by combining the polymer or admixture and other components under heat to yield a feedstock, thermoforming the feedstock in a mold to yield a foamed material sheet, and cutting the foamed material sheet.
Claims7
An elastomeric sanding block conformable to curved or flat surfaces, wherein the elastomeric sanding block has a Shore A hardness ranging from about 30 to about 90, and wherein the elastomeric sanding block is made from a composition comprising:
- an admixture of about 70 to about 90 weight percent of an ethylene-vinyl acetate copolymer and about 10 to about 30 weight percent of a low-density polyethylene homopolymer, wherein the admixture is in an amount that ranges from about 35 to about 70 weight percent of the composition;
- a blowing agent in an amount that ranges from about 1.5 to about 4.5 weight percent of the composition;
- and
- a pigment in an amount of about 5 weight percent to about 18 weight percent of the composition.
A method for manufacturing an elastomeric sanding block conformable to curved or flat surfaces, comprising the steps of:
- forming a composition comprising the steps of:
- forming an admixture comprising
- about 70 to about 90 weight percent of an ethylene-vinyl acetate copolymer and about 10 to about 30 weight percent of a low-density polyethylene homopolymer, wherein the admixture is in an amount that ranges from about 35 to about 70 weight percent of the composition;
- and
- combining the admixture with a pigment in an amount of about 5 percent to about 18 weight percent of the composition;
- combining the composition with a blowing agent under heat to yield a feedstock;
- thermoforming the feedstock in a mold to yield a foamed material sheet;
- and
- cutting the foamed material sheet to yield the elastomeric sanding block.
Dependencies are inferred from the claim text.