Loading patent…
AssigneeJfe Steel Corporation
InventorsYusuke Fushiwaki, Yoshiharu Sugimoto, Masahiro Yoshida, Yoshitsugu Suzuki
Estimating the term…
A method for producing a high-strength hot-dip galvanized steel sheet includes a steel sheet containing, in percent by mass, 0.01% to 0.18% of C, 0.02% to 2.0% of Si, 1.0% to 3.0% of Mn, 0.001% to 1.0% of Al, 0.005% to 0.060% of P, 0.01% or less of S, and the balance being Fe and incidental impurities, and a galvanized coating layer on each surface of the steel sheet with a coating weight of 20 to 120 g/m2 per surface, in which, when the steel sheet is subjected to annealing and a hot-dip galvanizing treatment in a continuous hot-dip galvanizing line, the dew point of the atmosphere is controlled to −40° C. or lower in the annealing furnace temperature range of 750° C. or higher.
A method for producing a high-strength hot-dip galvanized steel sheet including a steel sheet containing, in percent by mass, 0.01% to 0.18% of C, 0.02% to 2.0% of Si, 1.0% to 3.0% of Mn, 0.001% to 1.0% of Al, 0.005% to 0.060% of P, 0.01% or less of S, and the balance being Fe and incidental impurities, and a galvanized coating layer on each surface of the steel sheet with a coating weight of 20 to 120 g/m2 per surface, the method comprising, when the steel sheet is subjected to annealing and a hot-dip galvanizing treatment in a continuous hot-dip galvanizing line, controlling a dew point of the atmosphere to −40° C. or lower in every a region of the annealing furnace that has a temperature range higher than 780° C.
A method for producing a high-strength hot-dip galvanized steel sheet including a steel sheet containing, in percent by mass, 0.01% to 0.18% of C, 0.02% to 2.0% of Si, 1.0% to 3.0% of Mn, 0.001% to 1.0% of Al, 0.005% to 0.060% of P, 0.01% or less of S, and the balance being Fe and incidental impurities, and a galvanized coating layer on each surface of the steel sheet with a coating weight of 20 to 120 g/m2 per surface, the method comprising, when the steel sheet is subjected to annealing and a hot-dip galvanizing treatment in a continuous hot-dip galvanizing line, controlling a dew point of the atmosphere to −40° C. or lower in a region of the annealing furnace that has a temperature range higher than 780° C. during the annealing and hot-dip galvanizing treatment such that the amount of at least one oxide selected from oxides of Fe, Si, Mn, Al, P, B, Nb, Ti, Cr, Mo, Cu, and Ni, formed in the surface layer portion of the steel sheet, within 100 μm from the surface of the substrate steel sheet, directly below the galvanized coating layer, is 0.060 g/m2 or less per surface.
A method for producing a high-strength hot-dip galvanized steel sheet including a steel sheet containing, in percent by mass, 0.01% to 0.18% of C, 0.02% to 2.0% of Si, 1.0% to 3.0% of Mn, 0.001% to 1.0% of Al, 0.005% to 0.060% of P, 0.01% or less of S, and the balance being Fe and incidental impurities, and a galvanized coating layer on each surface of the steel sheet with a coating weight of 20 to 120 g/m2 per surface, the method comprising, when the steel sheet is subjected to annealing and a hot-dip galvanizing treatment in a continuous hot-dip galvanizing line, controlling a dew point of the atmosphere to −45° C. or lower in a region of the annealing furnace that has a temperature range higher than 780° C. during a heating step and a soaking step of the annealing and hot-dip galvanizing treatment.
Dependencies are inferred from the claim text.