Epoxy resin composition for resin transfer molding of fiber-reinforced composite material, fiber-reinforced composite material, and method for producing same

A process of producing a fiber-reinforced composite material with the epoxy resin composition for Resin Transfer Molding (RTM) of a fiber-reinforced composite material comprising [A] to [D] below, wherein [A]/[B], which is a blend mass ratio of [A] to [B], is 55/45 to 95/5:

• [A] a multifunctional epoxy resin that is liquid at normal temperature or has a softening point of 65° C. or lower, the multifunctional epoxy resin being at least one selected from the group consisting of phenol novolac epoxy resin, cresol novolac epoxy resin, and triphenylmethane epoxy resin;
• [B] an alicyclic epoxy resin;
• [C] an acid anhydride curing agent;
• [D] an organophosphorus compound or an imidazole having a substitute in its 1-position, and a reinforcing fiber, comprising steps (i) and (ii):
• (i) performing RTM molding in a mold at 90 to 130° C. for 0.5 to 10 minutes and performing mold release after bringing a glass-transition temperature to 95 to 150° C. and a reaction rate to 50 to 90% to obtain a pre-molded product;
• and
• (ii) post-curing the obtained pre-molded product in a temperature range of 130 to 200° C. to obtain a fiber-reinforced composite material whose glass-transition temperature has been brought to 150 to 220° C. and reaction rate to 90 to 100%.