Powder comprising ceramic granules and low Tg binder

A powder comprising granules which is intended in particular for the production of ceramic sintered parts, said powder having the following chemical composition by weight, on the basis of the dry matter:

• a ceramic material chosen in the group consisting in silicon carbide, silicon nitride and mixtures thereof, and, optionally, a stabilizer for said ceramic material:
• to make up 100%;
• at least 1.0% of a first binder having a glass transition temperature of less than or equal to 15° C.;
• 0 to 4.0% of an additional binder having a glass transition temperature of greater than 25° C.;
• 0 to 4.0% of a temporary additive different from a first binder and from an additional binder, the total content of said first binder, of said additional binder and of said temporary additive being less than 9.0%;
• 0 to 15% of an additive for sintering the ceramic material;
• less than 2.0% of impurities;
• the median diameter D50 of the powder being between 80 and 130 μm, the percentile D995 being less than 500 μm, the 10 percentile D10 is greater than 40 μm and the relative density of the granules being between 30% and 60%.