US 9,284,983 B2Granted
Raceway element for a large roller bearing and bearing assembly
AssigneeAktiebolaget Skf
InventorsBaozhu Liang, Ulrike May, Gerhard Wagner, Claus Rumpel
Life of this patent
Estimating the term…
Abstract
A roller bearing element for a large roller bearing includes the following features: at least one contact zone for a roller bearing counter element, the contact zone has an induction-hardened surface layer, the roller bearing element is comprised of a steel, which includes an admixture of carbon of at least 0.46 mass %.
Claims5
A roller bearing element for use in a large roller bearing with an outer diameter of at least 250 millimeters, comprising:
- at least one contact zone configured to contact a counter element of the roller bearing,
- wherein:
- the contact zone has an induction-hardened surface layer,
- the roller bearing element is comprised of a steel, which includes an admixture of carbon of at least 0.46 mass %, and
- a maximum hardness of the induction-hardened surface layer is less than a maximum hardness of the steel,
- wherein the steel contains an admixture of molybdenum, and
- wherein the steel is 50CrMo4 and wherein the maximum hardness of the surface layer is substantially equal to a maximum hardness of 42CrMo4.
4 more elements
A method, comprising:
- forming at least one component of a roller bearing selected from an outer ring, an inner ring and a roller body from a steel having a carbon content of at least 0.46 mass % and containing an admixture of molybdenum, the roller bearing having an outer diameter of at least 250 millimeters, and
- induction hardening at least one contact surface of the at least one component such that a maximum hardness of the at least one contact surface is less than a maximum hardness of the steel,
- wherein the steel is 50CrMo4 and wherein hardening the at least one contact surface comprises hardening the at least one contact surface such that the hardness of the at least one contact surface is substantially equal to a maximum hardness of 42CrMo4.
A method, comprising:
- providing a steel having a carbon component of at least 0.46 mass % and having a maximum hardness;
- forming at least one component of a roller bearing selected from an outer ring, an inner ring and a roller body from the steel;
- and
- induction hardening at least one contact surface of the at least one component to a hardness that is less than the maximum hardness,
- wherein the steel is 50CrMo4 and wherein induction hardening the at least one contact surface comprises induction hardening the at least one contact surface to a hardness that is substantially equal to a maximum hardness of 42CrMo4.
2 more elements