Self-enhancement plastic profile and production method thereof

A method for producing a self-enhancement plastic profile, wherein said self-enhancement plastic profile comprises a PVC substrate and a fiberglass-containing PBT resin, wherein the PVC substrate resin and the fiberglass-containing PBT resin are co-extruded,

• wherein the PVC substrate comprises a PVC resin, a stabilizer, a modifier, a stain, a filler, a processing agent, and a pigment at mass fractions of 100, 3-8, 4-11, 3-6, 5-10, 1-4, and 0.015-0.045, respectively
• wherein the stabilizer is a lead based stabilizer, a calcium/zinc stabilizer or an organic tin stabilizer, the modifier is a CPE modifier or an acrylic ester modifier, the stain is titanium dioxide, the filler is kaolin, wollastonite, calcium carbonate or talc powder, the processing agent is acrylic ester, and the pigment is ultramarine or phthalocyanine blue;
• wherein the fiber-glass containing PBT resin forms one or more enhancement bars in the self-enhancement plastic profile, comprises 45-75% mass ratio of a PBT material and 25-55% mass ratio of fiberglass,
• the method comprising:
• employing a main extruder and an auxiliary extruder vertically arranged to the main extruder;
• extruding the PVC substrate using the main extruder and extruding the fiberglass-containing PBT resin using the auxiliary extruder simultaneously to form an extrudate;
• pre-profiling the extrudate;
• and
• cold-cutting the pre-profiled extrudate into a predetermined size,
• wherein the main extruder is a double screw plastic extruder comprising six heating zones, and an adapter, wherein temperatures of the heating zones are:
• zone I:
• 172-176° C., zone II:
• 175-180° C., zone III:
• 176-183° C., zone IV:
• 182-187° C., zone V:
• 184-190° C., zone VI:
• 172-176° C.,
• wherein a temperature in the adapter is 185-195° C.,
• wherein, in the main extruder, a rotating speed of an extrusion screw in the main engine is 7-9 rpm, and a rotating speed of a feeding screw is 18-25 rpm, a torque is:
• 32-39%, and a melting pressure is 310-330 bar;
• wherein the auxiliary extruder is a single screw extruder comprising three heating zone and an adapter, wherein temperatures of the heating zones are:
• zone I:
• 220-240° C., zone II:
• 220-240° C., zone III:
• 220-240° C., wherein the temperature in adapter is 220-240° C.,
• wherein the auxiliary extruder comprises two co-extrusion heads, wherein a heating temperature of a first co-extrusion head is 220-240° C., and a heating temperature of second co-extrusion head is 220-240° C., and
• wherein temperatures of a die head in the auxiliary extruder are:
• zone I:
• 185-200° C., zone II:
• 185-200° C., zone III:
• 185-200° C., and zone IV:
• 185-200° C.