PCVD method for manufacturing a primary preform for optical fibers
AssigneeDraka Comteq B.V.
InventorsIgor Milicevic, Mattheus Jacobus Nicolaas Van Stralen, Johannes Antoon Hartsuiker
Life of this patent
Estimating the term…
Abstract
A method for manufacturing a primary preform including providing a hollow substrate tube, supplying to the interior of the tube a main gas flow containing at least one glass-forming gas and at least one secondary gas flow containing at least one precursor for a dopant, creating a plasma reaction zone in the interior of the tube to effect deposition, and interrupting the supply of the at least one secondary gas flow near the reversal points of the supply and discharge sides of the substrate tube.
Claims16
A method for minimizing occurrence of glass layer fracture while manufacturing a primary preform for optical fibres using an internal plasma chemical vapour deposition process, comprising the steps of:
- i) providing a hollow glass substrate tube having a supply side and a discharge side;
- ii) supplying a gas flow to the interior of the hollow glass substrate tube via the supply side, the gas flow comprising:
- a) a continuous main gas flow comprising at least one glass-forming gas and
- b) a first secondary gas flow comprising at least one precursor for a dopant, being germanium, aluminum, phosphorus, and boron;
- iii) creating a plasma reaction zone in the interior of the hollow glass substrate tube using microwave radiation for effecting the deposition of glass layers on the inner surface thereof, the reaction zone moving back and forth along the longitudinal axis of the hollow glass substrate tube between a reversal point located near the supply side and a reversal point located near the discharge side, to obtain a substrate tube having glass layers deposited on the inner surface;
- and
- iv) intermittently interrupting by reducing or shutting off the supply of the first secondary gas flow comprising the at least one precursor for the dopant, being germanium, aluminum, phosphorus, and boron during step iii) when the plasma reaction zone is located near or at the reversal point located near the supply side and/or near or at the reversal point located near the discharge side to reduce or prevent the incorporation of the at least one precursor for the dopant in the glass of the preform at the supply side and/or discharge side to minimize glass layer fracture in the preform at the supply side and/or at the discharge side.
A method of minimizing occurrence of glass layer fracture while manufacturing a primary preform for optical fibres using an internal plasma chemical vapour deposition process, comprising the steps of:
- i) providing a hollow substrate tube having a supply side and a discharge side;
- ii) supplying a gas flow to the interior of the hollow substrate tube via the supply side, the gas flow comprising:
- a) a main gas flow comprising at least one glass-forming gas and
- b) a first secondary gas flow comprising at least one precursor for a dopant, being germanium, aluminum, phosphorus, and boron:
- iii) creating a plasma reaction zone in the interior of the hollow substrate tube using microwave radiation for effecting the deposition of glass layers on the inner surface thereof, the reaction zone moving back and forth along the longitudinal axis of the hollow substrate tube between a reversal point located near the supply side and a reversal point located near the discharge side, to obtain a substrate tube having glass layers deposited on the inner surface;
- iv) intermittently interrupting by reducing or shutting off the supply of the first secondary gas flow comprising the at least one precursor for the dopant, being germanium, aluminum, phosphorus, and boron during step iii) when the plasma reaction zone passes an interruption point near each of the supply side and the discharge side;
- and
- v) resuming the supply of the first secondary gas flow during step iii) when the plasma reaction zone passes a resumption point near each of the supply side and/or the discharge side to reduce or prevent the incorporation of the at least one precursor for the dopant in the glass of the reform at the supply side and/or discharge side to minimize glass layer fracture in the preform at the supply side and/or at the discharge side.
Dependencies are inferred from the claim text.