Hot gasket with stainless steel
AssigneeFederal-Mogul Corporation
InventorsJames Stout, Jonathan Youngman
Life of this patent
Estimating the term…
Abstract
A metal gasket for establishing a gas and fluid-tight seal between two members and which is resistant to temperatures of greater than 430° C. and even up to 540° C. is provided. The metal gasket is made of a 200 series stainless steel which includes, by weight percentage: up to 1.0% Silicon, 3.5-5.5% Manganese, up to 0.060% Phosphorus, up to 0.030% Sulfur, 17.5-19.5% Chromium, 0.50-2.00% Molybdenum, 4.0-6.0% Nickel, 0.10-1.00% Niobium, 0.08-0.30% Nitrogen and the remainder of Iron. This particular alloy has been found to provide the gasket with very high mechanical strength, even at temperatures of up to 540° C. Additionally, due to the low nickel content of the 200 series stainless steel, the metal gasket may be made more cost-effectively than other known metal gaskets.
Claims7
A gasket comprising:
- at least one layer made of metal and including an inner periphery that surrounds an opening;
- and
- wherein said metal is composed of up to 1.0% Silicon, 3.5-5.5% Manganese, up to 0.060% Phosphorus, up to 0.030% Sulfur, 17.5-19.5% Chromium, 0.50-2.00% Molybdenum, 4.0-6.0% Nickel, 0.10-1.00% Niobium, 0.08-0.30% Nitrogen and the remainder of Iron.
A method of making a gasket, comprising the steps of:
- preparing a sheet of metal that is composed of up to 1.0% Silicon, 3.5-5.5% Manganese, up to 0.060% Phosphorus, up to 0.030% Sulfur, 17.5-19.5% Chromium, 0.50-2.00% Molybdenum, 4.0-6.0% Nickel, 0.10-1.00% Niobium, 0.08-0.30% Nitrogen and the remainder of Iron;
- forming an opening in the sheet of metal;
- and
- forming an embossment bead in the sheet of metal circumferentially around the opening.