US 9,067,251 B2Granted

Method of forming an article from metal alloy sheet material

AssigneeGM Global Technology Operations LLC

InventorsJon T. Carter, Daniel George Valik

Life of this patent

Estimating the term…

Loading patent…

Abstract

A method of forming an article from a metal alloy sheet material includes stamping the metal alloy sheet material to thereby form a preform having at least one protrusion. The at least one protrusion includes a base portion, a first region having a first thickness and spaced apart from the base portion to thereby have a first maximum height, and a second region interconnecting the base portion and the first region and having a second thickness that is greater than the first thickness. After stamping, the method includes selectively annealing the second region without substantially annealing the first region, and, after selectively annealing, concurrently increasing the first maximum height and substantially equalizing the first thickness and the second thickness to thereby form the article.

Claims16

Dependent claims

A method of forming an article from a metal alloy sheet material, the method comprising:

stamping the metal alloy sheet material to thereby form a preform having at least one protrusion;
wherein the at least one protrusion includes a base portion, a first region having a first thickness and spaced apart from the base portion to thereby have a first maximum height, and a second region interconnecting the base portion and the first region and having a second thickness that is greater than the first thickness;
wherein the first region has a first hardness and the second region has a second hardness that is less than the first hardness;
concurrent to stamping:
straining the first region to a first strain level such that the first region has the first hardness;
and
straining the second region to a second strain level that is less than the first strain level such that the second region has the second hardness;
after stamping, selectively annealing the second region without substantially annealing the first region;
and
after selectively annealing, concurrently increasing the first maximum height, and substantially equalizing the first thickness and the second thickness to thereby form the article.

7 more elements

A method of forming an article from a metal alloy sheet material, the method comprising:

stamping the metal alloy sheet material to thereby form a preform having at least one protrusion, wherein the metal alloy sheet material is stamped with a stamping tool including a forming surface configured for shaping the metal alloy sheet material;
wherein the at least one protrusion has a longitudinal axis and includes;
a base portion;
a first region spaced apart from the base portion to thereby have a first maximum height along the longitudinal axis;
and
a second region extending from the base portion so as to interconnect the base portion and the first region, and having a second maximum height along the longitudinal axis that is less than the first maximum height;
wherein stamping the metal alloy sheet material includes stretching a first area of the metal alloy sheet material along the forming surface to form the corresponding first region of the at least one protrusion, and stretching a second area of the metal alloy sheet material along the forming surface to form the corresponding second region of the at least one protrusion;
wherein the first region has a first thickness and a first hardness, and wherein the second region has a second thickness that is greater than the first thickness, and a second hardness that is less than the first hardness;
concurrent to stamping:
straining the first region to a first strain level such that the first region has the first hardness;
and
straining the second region to a second strain level that is less than the first strain level such that the second region has the second hardness;
after stamping the metal alloy sheet material, selectively annealing only the second region without substantially annealing the first region to form a workpiece;
and
after selectively annealing, stamping the workpiece to concurrently increase the first maximum height, and substantially equalize the first thickness and the second thickness, to thereby form the article.

12 more elements

A method of forming an article from a metal alloy sheet material, the method comprising:

stamping the metal alloy sheet material to thereby form a preform having at least one protrusion, wherein the metal alloy sheet material is stamped with a stamping tool including a punch having a forming surface configured for shaping the metal alloy sheet material;
wherein the at least one protrusion has a longitudinal axis and includes;
a base portion;
a first region spaced apart from the base portion to thereby have a first maximum height along the longitudinal axis;
and
a second region extending from the base portion so as to interconnect the base portion and the first region, and having a second maximum height along the longitudinal axis that is less than the first maximum height;
wherein the metal alloy sheet material is an aluminum alloy in sheet form;
wherein stamping the metal alloy sheet material includes stretching a first area of the metal alloy sheet material along the forming surface to form the corresponding first region of the at least one protrusion, and stretching a second area of the metal alloy sheet material along the forming surface to form the corresponding second region of the at least one protrusion;
wherein the first region has a first thickness and a first hardness, and wherein the second region has a second thickness that is greater than the first thickness, and a second hardness that is less than the first hardness;
concurrent to stamping:
straining the first region to a first strain level such that the first region has the first hardness;
and
straining the second region to a second strain level that is less than the first strain level such that the second region has the second hardness;
after stamping the metal alloy sheet material, selectively annealing only the second region without substantially annealing the first region to form a workpiece, wherein selectively annealing includes induction heating the metal alloy sheet material to a temperature of from 300° C. to 400° C. for a duration of from 5 seconds to 30 seconds;
after selectively annealing, quenching the workpiece to ambient temperature;
after quenching the workpiece, stamping the workpiece to concurrently increase the first maximum height, and substantially equalize the first thickness and the second thickness, to thereby form the article;
and
concurrent to stamping the workpiece, preferentially inducing comparatively more deformation at the second region than at the first region so that the article has a substantially uniform thickness of from 1 mm to 2 mm at each of the first region and the second region.