# US 9,038,704 B2 · Aluminum alloy compositions and methods for die-casting thereof > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 9,038,704 B2 - Document ID: US9038704B2 - Status: Granted - Kind: B2 - Application number: 13/438,525 - Filed: 2012-04-03 - Published: 2012-11-01 - Granted: 2015-05-26 - Earliest claimed: 2011-04-04 - Assignees: Emerson Climate Technologies, Inc. - Applicants: Warren G. Williamson - Inventors: Warren G. Williamson - Web page: https://patentgrep.com/patent/US9038704B2 ## CPC - B22D 21/04: Casting aluminium or magnesium {(no material; see B22D21/007)} - B23K 35/286: {Al as the principal constituent} - C22C 21/02: with silicon as the next major constituent - C22C 21/04: Modified aluminium-silicon alloys - B22D: CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES (shaping of plastics or substances in a plastic state B29C; metallurgical processing, selection of substances to be added to metal C21, C22) - B23K: SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM - C22C: ALLOYS (treatment of alloys C21D, C22F) ## Abstract Aluminum alloys are provided that have improved fluidity and elongation, as well as freedom of die soldering. The aluminum alloys are particularly suitable for die-casting of structural components. The aluminum alloy includes silicon at from about 8 weight % to about 11 weight %, manganese at from about 0.8 weight % to about 1.9 weight %, iron at from about 0.1 weight % to about 0.5 weight %, magnesium at from about 0.2 weight % to about 0.7 weight %, boron at from about 0.002 weight % to about 0.15 weight %, strontium at from about 0.006 weight % to about 0.017 weight %, less than about 0.25 weight % copper, less than about 0.35 weight % zinc, less than about 0.25 weight % titanium, and a balance of aluminum. Methods related to the aluminum alloys are also provided. ## Claims ### Claim 1 A method of forming a structural compressor component for a compressor comprising: casting a molten aluminum alloy material to form a solid structural compressor component, wherein the aluminum alloy material comprises: silicon at greater than about 8 weight % to less than 10 weight % of the aluminum alloy material; manganese at greater than or equal to about 0.8 weight % to less than or equal to about 1.9 weight % of the aluminum alloy material; iron at greater than or equal to about 0.1 weight % to less than or equal to about 0.5 weight % of the aluminum alloy material; magnesium at greater than or equal to about 0.2 weight % to less than or equal to about 0.7 weight % of the aluminum alloy material; boron at greater than or equal to about 0.002 weight % to less than or equal to about 0.15 weight % of the aluminum alloy material; strontium at greater than or equal to about 0.006 weight % to less than or equal to about 0.017 weight % of the aluminum alloy material; less than or equal to about 0.25 weight % copper of the aluminum alloy material; less than or equal to about 0.35 weight % zinc of the aluminum alloy material; less than or equal to about 0.25 weight % titanium of the aluminum alloy material; and a balance of the aluminum alloy material being aluminum; annealing the solid structural compressor component by exposure to a heat source having a holding temperature of greater than or equal to about 500° F. to less than or equal to about 800° F. for greater than or equal to five hours to less than or equal to 24 hours, wherein after the annealing, the solid structural compressor component has a hardness of greater than or equal to about 75 to less than or equal to about 90 HRH (Rockwell Hardness H Scale) and a percentage of elongation of greater than or equal to 7%; and machining the solid structural compressor component for incorporation into the compressor. ### Claim 2 (depends on 1) The method of claim 1, wherein the structural compressor component has a percentage of elongation of greater than or equal to about 9%. ### Claim 3 (depends on 1) The method of claim 1, wherein the structural compressor component has a tensile strength of greater than or equal to about 38,000 psi. ### Claim 4 (depends on 1) The method of claim 1, wherein the structural compressor component has a tensile strength of greater than or equal to about 40,000 psi. ### Claim 5 (depends on 1) The method of claim 1, wherein the aluminum alloy material comprises nickel at no greater than a trace impurity amount of less than or equal to about 0.05 weight % of the aluminum alloy material. ### Claim 6 (depends on 1) The method of claim 1, wherein the casting is a die-casting process where the molten aluminum alloy material passes through a die during the casting process. ### Claim 7 (depends on 1) The method of claim 1, wherein the manganese comprises greater than or equal to 1 to less than or equal to 1.2 weight % of the aluminum alloy material. ### Claim 8 A method of forming a structural compressor component for a compressor comprising: a. die-casting an aluminum alloy comprising a synergistic amount of manganese and silicon comprising greater than or equal to about 1 weight % to less than or equal to about 1.2 weight % of manganese in the aluminum alloy and from greater than or equal to about 9 weight % to less than or equal to about 10 weight % silicon in the aluminum alloy; b. solidifying the aluminum alloy to form the structural compressor component, wherein the solidified aluminum alloy has an elongation of greater than or equal to 7% and a tensile strength of greater than or equal to 38,000 psi; c. heating the solid structural compressor component by exposure to a heat source having a rate of heating of greater than or equal to about 50° F. per hour to less than or equal to about 200° F. per hour to reach a holding temperature; and d. annealing the aluminum alloy for greater than or equal to five hours to less than or equal to 24 hours at the holding temperature of greater than or equal to about 500° F. to less than or equal to about 800° F., so that the solid structural compressor component has a hardness of greater than or equal to about 75 to less than or equal to about 90 HRH (Rockwell Hardness H Scale). ### Claim 9 (depends on 8) The method of claim 8, wherein the aluminum alloy further comprises: iron at greater than or equal to about 0.1 weight % to less than or equal to about 0.5 weight % of the aluminum alloy; magnesium at greater than or equal to about 0.2 weight % to less than or equal to about 0.7 weight % of the aluminum alloy; boron at greater than or equal to about 0.002 weight % to less than or equal to about 0.15 weight % of the aluminum alloy; strontium at greater than or equal to about 0.006 weight % to less than or equal to about 0.017 weight % of the aluminum alloy; less than or equal to about 0.25 weight % copper of the aluminum alloy; less than or equal to about 0.35 weight % zinc of the aluminum alloy; less than or equal to about 0.25 weight % titanium of the aluminum alloy; and a balance of the aluminum alloy being aluminum. ### Claim 10 (depends on 9) The method of claim 9, wherein the aluminum alloy comprises nickel at no greater than a trace impurity amount of less than or equal to about 0.05 weight % of the aluminum alloy. ### Claim 11 (depends on 9) The method of claim 9, wherein the aluminum alloy comprises copper at no greater than a trace impurity amount of less than or equal to about 0.05 weight % of the aluminum alloy. ### Claim 12 (depends on 8) The method of claim 8, wherein the elongation is greater than or equal to 9%. ### Claim 13 (depends on 8) The method of claim 8, wherein the tensile strength is greater than or equal to 40,000 psi. ### Claim 14 (depends on 8) The method of claim 8, wherein the annealing occurs at a temperature of about 600° F. to about 700° F. ### Claim 15 (depends on 8) The method of claim 8, wherein the rate of heating is greater than or equal to about 100° F. per hour to less than or equal to about 150° F. per hour. ### Claim 16 (depends on 8) The method of claim 8, wherein the annealing at the holding temperature occurs for greater than or equal to about 8 hours to less than or equal to about 10 hours. ### Claim 17 A method of forming a structural scroll compressor component for a scroll compressor comprising: casting a molten aluminum alloy material to form a solid scroll compressor structural component, wherein the aluminum alloy material comprises: silicon at greater than or equal to about 8 weight % to less than or equal to about 10 weight % of the aluminum alloy material; manganese at greater than 1 weight % to less than or equal to about 1.9 weight % of the aluminum alloy material; iron at greater than or equal to about 0.1 weight % to less than or equal to about 0.5 weight % of the aluminum alloy material; magnesium at greater than or equal to about 0.2 weight % to less than or equal to about 0.7 weight % of the aluminum alloy material; boron at greater than or equal to about 0.002 weight % to less than or equal to about 0.15 weight % of the aluminum alloy material; strontium at greater than or equal to about 0.006 weight % to less than or equal to about 0.017 weight % of the aluminum alloy material; less than or equal to about 0.25 weight % copper of the aluminum alloy material; less than or equal to about 0.35 weight % zinc of the aluminum alloy material; less than or equal to about 0.25 weight % titanium of the aluminum alloy material; and a balance of the aluminum alloy material being aluminum; annealing the solid scroll compressor structural component by exposure to a heat source having a holding temperature of greater than or equal to about 500° F. to less than or equal to about 800° F. for greater than or equal to five hours to less than or equal to 24 hours, wherein after the annealing, the solid scroll compressor structural component has a hardness of greater than or equal to about 75 to less than or equal to about 90 HRH (Rockwell Hardness H Scale) and a percentage of elongation of greater than or equal to 7%; and machining the solid scroll compressor structural component for incorporation into the scroll compressor.