Blow molding ethylene resin composition and blow molded article therefrom

A fuel tank comprising a blow molded article that comprises a layer comprising a blow molding ethylene resin composition;

• wherein the blow molding ethylene resin composition comprises a single or two or more ethylene polymers in the range of 99 wt % or more, wherein the ethylene polymer satisfies the following requirements [1] and [2] at the same time, and wherein the ethylene resin composition satisfies the following requirements [a], [b], [c], [d] and [h] at the same time:
• [1] the ethylene polymer is prepared by a process comprising synthesizing an ethylene homopolymer in an amount corresponding to 50 to 65 wt % based on the final polymer, and synthesizing an ethylene/α-olefin copolymer in an amount corresponding to 35 to 50 wt % based on the final polymer;
• [2] the intrinsic viscosity [η] of the ethylene homopolymer measured at 135° C. in a decalin solution is in the range of 1.01 to 1.5 (dl/g);
• [a] the melt flow rate (MFR) at a temperature of 190° C. under a load of 21.6 kg is in the range of 1.0 to 10 g/10 min;
• [b] the density is in the range of 955 to 960 kg/m3;
• [c] the number of methyl branches per 1000 carbon atoms is less than 0.1 according to 13C-NMR;
• [d] the tensile impact strength measured at −40° C. in accordance with JIS K 7160 is not less than 270 kJ/m2;
• [h] the intrinsic viscosity [η] measured at 135° C. in a decalin solution is in the range of 3.0 to 5.0 (dl/g).