# US 8,999,743 B2 · Manufacture of solar cell module > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 8,999,743 B2 - Document ID: US8999743B2 - Status: Granted - Kind: B2 - Application number: 14/320,790 - Filed: 2014-07-01 - Published: 2015-01-08 - Granted: 2015-04-07 - Earliest claimed: 2013-07-04 - Assignees: Shin-Etsu Chemical Co., Ltd. - Applicants: Shin-Etsu Chemical Co., Ltd. - Inventors: Tomoyoshi Furihata; Hiroto Ohwada; Naoki Yamakawa; Masahiro Hinata - Web page: https://patentgrep.com/patent/US8999743B2 ## CPC - H10F 19/807: {Double-glass encapsulation, e.g. photovoltaic cells arranged between front and rear glass sheets} - H10F 19/80: Encapsulations or containers for integrated devices, or assemblies of multiple devices, having photovoltaic cells - Y02E 10/50: Photovoltaic [PV] energy - H10F: INORGANIC SEMICONDUCTOR DEVICES SENSITIVE TO INFRARED RADIATION, LIGHT, ELECTROMAGNETIC RADIATION OF SHORTER WAVELENGTH OR CORPUSCULAR RADIATION - Y02E: REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION ## Abstract A solar cell module is manufactured by forming silicone coating films (2, 2) on panels (1a, 1b), placing a solar cell matrix (3) on the silicone coating film on panel (1a), providing a seal member (4) consisting of a base seal member (4a) of butyl rubber and protrusive seal segments (4b) of butyl rubber on a peripheral region of panel (1a), mating the two panels together such that the seal member (4) may abut against a peripheral region of panel (1b), and the solar cell matrix (3) may be sandwiched between the silicone coating films (2), and compressing and heating the mated panels (1a, 1b) in vacuum for establishing a seal around the solar cell matrix (3). ## Claims ### Claim 1 A method for manufacturing a solar cell module by resin encapsulating a solar cell matrix comprising a plurality of electrically connected solar cell components between two panels, comprising the steps of: (i) forming a silicone coating film on one surface of each of two panels, excluding a peripheral region of the one surface, (ii) placing the solar cell matrix on the silicone coating film on one panel, such that in case the solar cell component is of monofacial light receiving type, the light receiving side may face upward, and in case the solar cell component is of bifacial light receiving type, either one light receiving side may face upward, (iii) providing a base seal member on the peripheral region of the silicone coating film-bearing surface of either one panel where the silicone coating film is not formed, said seal member comprising a butyl rubber-based thermoplastic sealing material and being thicker than the silicone coating film on the panel, such that a ratio of the volume (V2) of the base seal member to the volume (V1) of a seal portion, which is given as the total thickness of the silicone coating films on the panels multiplied by the width of the peripheral region of the surface of the base seal member-bearing panel where the silicone coating film is not formed, may range from 1.2/1 to 1.5/1, and then providing protrusive seal segments on the base seal member at four or more spaced-apart positions, said protrusive seal segments comprising a butyl rubber-based thermoplastic sealing material and having a height of 1 to 4 mm, (iv) mating the two panels together such that the silicone coating film-bearing surface of the panel on which the solar cell matrix is not placed may be opposed to the solar cell matrix, a seal member consisting of the base seal member and protrusive seal segments may abut against a peripheral region of the panel on which the seal member is not provided where the silicone coating film is not formed, and the solar cell matrix may be sandwiched between the silicone coating films, (v) evacuating a space in which the mated panels are placed to vacuum, compressing and heating the mated panels in vacuum for establishing a seal around the solar cell matrix. ### Claim 2 (depends on 1) The method of claim 1 wherein step (iii) includes previously forming the base seal member in tape form and the protrusive seal segments, placing the base seal member on the peripheral region of the silicone coating film-bearing surface of either one panel where the silicone coating film is not formed, and then placing the protrusive seal segments on the base seal member at four or more spaced-apart positions. ### Claim 3 (depends on 1) The method of claim 1 wherein step (iii) includes previously forming the base seal member in tape form and the protrusive seal segments, placing the protrusive seal segments on the base seal member at four or more spaced-apart positions to form a seal member, and then placing the seal member on the peripheral region of the silicone coating film-bearing surface of either one panel where the silicone coating film is not formed. ### Claim 4 (depends on 1) The method of claim 1 wherein the silicone coating film is a silicone gel film formed by coating and curing a curable silicone gel composition and having a penetration of 30 to 200 as measured according to JIS K2220. ### Claim 5 (depends on 1) The method of claim 1 wherein the silicone coating film has a thickness of 200 to 1,000 μm. ### Claim 6 (depends on 1) The method of claim 1 wherein step (v) includes heating the mated panels in vacuum at a temperature of 70 to 120° C. ### Claim 7 (depends on 1) The method of claim 1 wherein step (v) is carried out using a vacuum laminator. ### Claim 8 (depends on 1) The method of claim 1 wherein at least one of the two panels is a transparent plate. ### Claim 9 A method for manufacturing a solar cell module by resin encapsulating a solar cell matrix comprising a plurality of electrically connected solar cell components between two panels, comprising the steps of: (i) forming a silicone coating film on one surface of each of two panels, excluding a peripheral region of the one surface, (ii) placing a solar cell matrix on the silicone coating film on one panel, such that in case the solar cell component is of monofacial light receiving type, the light receiving side may face upward, and in case the solar cell component is of bifacial light receiving type, either one light receiving side may face upward, (iii) providing a base seal member on the peripheral region of the silicone coating film-bearing surface of either one panel where the silicone coating film is not formed, said seal member comprising a butyl rubber-based thermoplastic sealing material and being thicker than the silicone coating film, such that a ratio of the volume (V2) of the base seal member to the volume (V1) of a seal portion, which is given as the total thickness of the silicone coating films on the panels multiplied by the width of the peripheral region of the surface of the base seal member-bearing panel where the silicone coating film is not formed, may range from 1.2/1 to 1.5/1, and providing protrusive seal segments on the peripheral region of the silicone coating film-bearing surface of the other panel where the silicone coating film is not formed, at four or more spaced-apart positions, said protrusive seal segments comprising a butyl rubber-based thermoplastic sealing material and having a height of 1 to 4 mm, (iv) mating the two panels together such that the silicone coating film-bearing surface of the panel on which the solar cell matrix is not placed may be opposed to the solar cell matrix, the protrusive seal segments may abut against the base seal member, and the solar cell matrix may be sandwiched between the silicone coating films, (v) evacuating a space in which the mated panels are placed to vacuum, compressing and heating the mated panels in vacuum for establishing a seal around the solar cell matrix. ### Claim 10 (depends on 9) The method of claim 9 wherein step (iii) includes previously forming the base seal member in tape form and the protrusive seal segments, placing the base seal member on the peripheral region of the silicone coating film-bearing surface of either one panel where the silicone coating film is not formed, and placing the protrusive seal segments on the peripheral region of the silicone coating film-bearing surface of the other panel where the silicone coating film is not formed, at four or more spaced-apart positions.