Bond coating powder comprising MCrAlY (M=Ni,Fe,Co), method of making, and a method of applying as bond coating
AssigneeGeneral Electric Company
InventorsArunkumar Shamrao Watwe, Yuk-Chiu Lau
Life of this patent
Estimating the term…
Abstract
Provided is bond coating powder and method of making. The method includes providing a powder including a plurality of parent particles. The method includes providing a plurality of dispersoids. The method includes mechanically alloying the powder and the plurality of dispersoids at ambient temperature. The mechanical alloying operable to provide a selective occupation of the plurality of dispersoids in a grain boundary area of the plurality of parent particles providing the bond coating powder. The plurality of dispersoids occupy about 18 percent to about 30 percent of the grain boundary area of the bond coating powder.
Claims18
A method of making a bond coating powder comprising:
- providing a powder including a plurality of parent particles selected from the group consisting of MCrAlY, wherein M is Ni, Fe, Co, and combinations thereof;
- providing a plurality of dispersoids;
- and
- mechanically alloying the plurality of parent particles and the plurality of dispersoids at ambient temperature, the mechanical alloying being operable to provide a selective occupation by the plurality of dispersoids in a grain boundary area of the plurality of parent particles of the bond coating powder;
- wherein the plurality of dispersoids occupy about 18 percent to about 30 percent of the grain boundary area;
- and
- wherein the plurality of dispersoids selectively occupying the grain boundary area of the plurality of parent particles include a property of reducing a rate of aluminum depletion from the bond coating powder relative to a comparable bond coating lacking the plurality of dispersoids.
A bond coating powder comprising:
- a plurality of parent particles selected from the group consisting of MCrAlY, wherein M is Ni, Fe, Co, and combinations thereof;
- and
- a plurality of dispersoids mechanically alloyed with the plurality of parent particles forming the bond coating powder, wherein the plurality of dispersoids selectively occupy a grain boundary area of the plurality of parent particles providing a bond coating powder;
- wherein the plurality of dispersoids occupy from about 18 percent to about 30 percent of the grain boundary area;
- and
- wherein the plurality of dispersoids selectively occupying the grain boundary area of the plurality of parent particles include a property of reducing a rate of aluminum depletion from the bond coating powder relative to a comparable bond coating lacking the plurality of dispersoids.
A method of applying a bond coating to a component comprising:
- providing a bond coating powder including a plurality of parent particles selected from the group consisting of MCrAlY, wherein M is Ni, Fe, Co, and combinations thereof;
- providing a plurality of dispersoids;
- mechanically alloying the plurality of parent particles and the plurality of dispersoids at ambient temperature, the mechanically alloying being operable to provide a selective occupation by the plurality of dispersoids in a grain boundary area of the plurality of particles of the bond coating powder, the plurality of dispersoids occupying about 18 percent to about 30 percent of the grain boundary area;
- applying the bond coating powder to the component, wherein a bond coating forms on the metallic component, wherein the plurality of dispersoids selectively occupying the grain boundary area of the plurality of parent particles include a property of reducing a rate of aluminum depletion from the bond coating powder to an adjacent bond coat and thermal barrier coating interface relative to a comparable bond coating lacking the plurality of dispersoids.
Dependencies are inferred from the claim text.