Polyethylene terephthalate resin synthesized inorganic Ti—Mg catalyst and its applications thereof
AssigneeNan Ya Plastics Corporation
InventorZo-Chun Jen
Life of this patent
Estimating the term…
Abstract
PET resins containing a small amount of a blue dye and/or further containing inorganic particles of Fe3O4 or BaSO4 are synthesized in the presence of an inorganic Ti—Mg catalyst employed as a polycondensation catalyst and a phosphorus stabilizer during a polycondensation process, and the resultant PET resins are free of yellowish appearance and reduced regenerated acetaldehyde and cyclic oligomers after processed so that PET bottle preforms if made of the PET resins can facilitate reduction in aging time thereby to improve the product yield of the bottle preforms and to save the stock space for storing the bottle preforms.
Claims11
A polyethylene terephthalate resin containing polyethylene terephthalate (PET), a blue dye in an amount of 0.5 to 2.0 ppm based on the total PET resin weight and inorganic particles of Fe3O4 having a particle size smaller than 1 μm in an amount of ranging from 20 to 250 ppm based on the total PET resin weight, which is produced by following steps:
- (a) using purified terephthalic acid (PTA) and ethylene glycol (EG) to undergo a direct esterification process and a polycondensation process successively, or selectively further to undergo a solid-state polymerization process to increase an intrinsic viscosity of the PET polymer to 0.70 dl/g or more,
- (b) before the end of the direct esterification process the blue dye and the inorganic particles of Fe3O4 are added into a reaction tank where the direct esterification process takes place, and
- (c) before the beginning of the polycondensation process an inorganic Ti—Mg catalyst having a particle size smaller than 1 μm and a phosphorus compound as a stabilizer added into the reaction tank, wherein the inorganic Ti—Mg catalyst is synthesized by chemical precipitation comprising the following steps:
- (i) taking TiCl4 dissolved in deionized water and then undergoing a hydrolysis process in an ice water bath to form an aqueous hydrolyzate solution;
- (ii) mixing the aqueous hydrolyzate solution with an aqueous MgCl2 solution at a predetermined molar ratio (Ti/Mg) of titanium (Ti) to magnesium (Mg) at room temperature;
- (iii) slowly adding an aqueous NaOH solution into the constantly stirred Ti—Mg mixture to form a kind of slurry containing a white precipitate;
- (iv) washing the slurry with deionized water, and then filtered and vacuum dried at 100° C.;
- (v) pulverizing the dried product into powders sized under 1 μm;
- and taking the resultant powders mixed with ethylene glycol to produce the inorganic Ti—Mg catalyst solution;
- wherein the inorganic Ti—Mg catalyst is added in an amount of ranging from 10 to 100 ppm and the phosphorus compound is added in amount of ranging from 5 to 50 ppm based on the total PET resin weight, and wherein the titanium contained in the Ti—Mg catalyst ranges from 5 to 10 ppm based on the total PET resin weight, and the molar ratio (Ti/Mg) of titanium (Ti) to magnesium (Mg) ranges from about 0.005 to 0.25.