Methods for manufacturing a calcined gypsum and a gypsum board
AssigneeYoshino Gypsum Co., Ltd.
InventorShizuo Taira
Life of this patent
Estimating the term…
Abstract
The present invention provides a method for manufacturing a calcined gypsum wherein the mixing water amount is reduced and the setting time does not increase. As a raw gypsum is compounded with a carboxylic acid-type material and calcined, a calcined gypsum can be manufactured wherein the mixing water amount is small and the setting time does not increase. Furthermore, a regular gypsum board can be manufactured without reducing the productivity of the gypsum board even if a large quantity of recycled gypsum causing increase of the mixing water amount is used as a raw gypsum, because the mixing water amount is small and the setting time does not increase for the calcined gypsum manufactured as described above.
Claims9
A method for manufacturing a baked gypsum product, consisting of:
- a step of compounding a raw gypsum with a carboxylic acid-type material to obtain a mixture of the raw gypsum and the carboxylic acid-type material, a ratio of the carboxylic acid-type material to the raw gypsum being within a range of 0.01 wt % to 10 wt % per the raw gypsum, the raw gypsum being in 90 wt % of 100 mesh pass;
- a step of baking the mixture by using a kettle or a rotary kiln to obtain a baked gypsum;
- a step of cooling the baked gypsum to obtain a cooled gypsum;
- and
- a step of pulverizing the cooled gypsum to obtain a baked gypsum product, an amount of water to be mixed into the baked gypsum product being within a range of 61 wt % to 87 wt %,
- wherein the carboxylic acid-type material includes at least one selected from the group consisting of malic acid and salts thereof, citric acid and salts thereof, tartaric acid and salts thereof, maleic acid and salts thereof, and gluconic acid and salts thereof.
Dependencies are inferred from the claim text.