Loading patent…
AssigneeKaneka Corporation
InventorsHirofumi Inari, Katsuyuki Tanaka, Kimihide Nishimura
Estimating the term…
The present invention provides a (meth)acrylic resin composition comprising a carboxylic acid group produced by heating a (meth)acrylic-based resin (C), wherein the (meth)acrylic-based resin (C) is obtained by polymerizing a monomer mixture (A) containing 80 to 99 wt % of a linear alkyl (meth)acrylate and 1 to 20 wt % of tertiary-butyl (meth)acrylate, in the presence of an acrylic acid ester-based crosslinked elastic particle (B) that is obtained by mixing and polymerizing 0.5 to 5 parts by weight of a polyfunctional monomer having at least two non-conjugated double bonds per molecule, with respect to 100 parts by weight of a monomer mixture containing 50 to 100 wt % of an alkyl acrylate monomer and 0 to 50 wt % of an alkyl methacrylate monomer. This composition can be used to produce a film having excellent chemical resistance (in particular, sun-screening agent resistance).
An imidized (meth)acrylic resin composition obtained by imidizing a (meth)acrylic resin composition obtained by heating a (meth)acrylic-based resin (C), wherein the (meth)acrylic-based resin (C) is obtained by polymerizing a monomer mixture (A) containing 80 to 99 wt % of a linear alkyl (meth)acrylate and 1 to 20 wt % of tertiary-butyl (meth)acrylate, in the presence of an alkyl acrylate-based crosslinked elastic particle (B) that is obtained by mixing and polymerizing 0.5 to 5 parts by weight of a polyfunctional monomer having at least two non-conjugated double bonds per molecule, with respect to 100 parts by weight of a monomer mixture containing 50 to 100 wt % of an alkyl acrylate monomer and 0 to 50 wt % of an alkyl methacrylate monomer.
A film obtained by molding an imidized (meth)acrylic resin composition obtained by imidizing a (meth)acrylic resin composition obtained by heating a (meth)acrylic-based resin (C), wherein the (meth)acrylic-based resin (C) is obtained by polymerizing a monomer mixture (A) containing 80 to 99 wt % of a linear alkyl (meth)acrylate and 1 to 20 wt % of tertiary-butyl (meth)acrylate, in the presence of an alkyl acrylate-based crosslinked elastic particle (B) that is obtained by mixing and polymerizing 0.5 to 5 parts by weight of a polyfunctional monomer having at least two non-conjugated double bonds per molecule, with respect to 100 parts by weight of a monomer mixture containing 50 to 100 wt % of an alkyl acrylate monomer and 0 to 50 wt % of an alkyl methacrylate monomer.
A laminated product obtained by laminating a metal or a plastic with a film obtained by molding an imidized (meth)acrylic resin composition obtained by imidizing a (meth)acrylic resin composition obtained by heating a (meth)acrylic-based resin (C), wherein the (meth)acrylic-based resin (C) is obtained by polymerizing a monomer mixture (A) containing 80 to 99 wt % of a linear alkyl (meth)acrylate and 1 to 20 wt % of tertiary-butyl (meth)acrylate, in the presence of an alkyl acrylate-based crosslinked elastic particle (B) that is obtained by mixing and polymerizing 0.5 to 5 parts by weight of a polyfunctional monomer having at least two non-conjugated double bonds per molecule, with respect to 100 parts by weight of a monomer mixture containing 50 to 100 wt % of an alkyl acrylate monomer and 0 to 50 wt % of an alkyl methacrylate monomer.
Dependencies are inferred from the claim text.