Gallium electrodeposition processes and chemistries
AssigneeInternational Business Machines Corporation
InventorsShafaat Ahmed, Hariklia Deligianni
Life of this patent
Estimating the term…
Abstract
Solutions and processes for electrodepositing gallium or gallium alloys includes a plating bath free of complexing agents including a gallium salt, an indium salt, a combination thereof, and a combination of any of the preceding salts with copper, an acid, and a solvent, wherein the pH of the solution is in a range selected from the group consisting of from about zero to about 2.6 and greater than about 12.6 to about 14. An optional metalloid may be included in the solution.
Claims8
A method for electrodepositing a substrate, the method comprising:
- contacting (i) a solution consisting of a metal salt, wherein the metal salt consists of a metal selected from the group consisting of gallium, and a combination of gallium with copper;
- methane sulfonic acid;
- an inorganic metalloid compound selected from the group consisting of arsenic, antimony, bismuth, and a combination thereof;
- and further optionally an organic additive having at least one sulfur atom;
- and a solvent to dissolve said metal salt, wherein the solution is free of a complexing agent;
- and (ii) a substrate;
- adjusting pH of the solution to a range selected from the group consisting of from about zero to about 2.6 and greater than about 12.6 to about 14;
- and
- applying a current to electroplate the substrate with a metal film consisting essentially of gallium or the combination of gallium and copper, wherein the substrate comprises one or more alloying element metal layers and the method further comprises annealing subsequent to electroplating the metal film.
A method for electrodepositing a substrate, the method comprising:
- contacting (i) a solution consisting of a metal salt, wherein the metal salt consists of a metal selected from the group consisting of gallium, and a combination of gallium with copper;
- methane sulfonic acid;
- an inorganic metalloid compound selected from the group consisting of arsenic, antimony, bismuth, and a combination thereof;
- and a solvent to dissolve said metal salt, wherein the solution is free of a complexing agent;
- and (ii) a substrate;
- adjusting pH of the solution to a range selected from the group consisting of from about zero to about 2.6 and greater than about 12.6 to about 14;
- and
- applying a current to electroplate the substrate with a metal containing film.
A method for electrodepositing a substrate, the method comprising:
- contacting (i) a solution consisting of a metal salt, wherein the metal salt consists of a metal selected from the group consisting of gallium, and a combination of gallium with copper;
- methane sulfonic acid;
- an inorganic metalloid compound selected from the group consisting of arsenic, antimony, bismuth, and a combination thereof;
- an organic additive having at least one sulfur atom;
- and a solvent to dissolve said metal salt, wherein the solution is free of a complexing agent;
- and (ii) a substrate;
- adjusting pH of the solution to a range selected from the group consisting of from about zero to about 2.6 and greater than about 12.6 to about 14;
- and
- applying a current to electroplate the substrate with a metal containing film.
Dependencies are inferred from the claim text.